Method for reproducing polyester container and reproduced polyester chip prepared therefrom
A process for regenerating a polyester container and regenerated polyester chips prepared therefrom. The process comprises preparing a polyester container provided with a heat shrinkable film; crushing the container provided with the heat shrinkable film to obtain flakes; and thermally treating the flakes to produce regenerated polyester chips, wherein when the flakes are thermally treated at a temperature of 200° C. to 220° C. for 60 minutes to 120 minutes, the clumping fraction is 5% or less, and the flakes comprise first flakes obtained by crushing the container and second flakes obtained by crushing the heat shrinkable film. It not only solves the environmental problems by improving the recyclability of the polyester container, but also is capable of enhancing the yield and productivity.
1. A process for regenerating a polyester container, which comprises preparing the polyester container provided with a heat shrinkable film comprising a copolymerized polyester resin comprising a diol component and a dicarboxylic acid component;
crushing the container provided with the heat shrinkable film to obtain flakes; and
thermally treating the flakes to produce regenerated polyester chips,
wherein when the flakes are thermally treated at a temperature of 200° C. to 220° C. for 60 minutes to 120 minutes, the clumping fraction is 5% or less; and
the flakes comprise first flakes obtained by crushing the container and second flakes obtained by crushing the heat shrinkable film.
2. The process for regenerating a polyester container of claim 1 , wherein the particle size of the first flakes is 0.1 to 20 mm, and the particle size of the second flakes is 0.1 to 20 mm.
3. The process for regenerating a polyester container of claim 1 , which comprises washing the flakes prior to the thermal treatment of the flakes.
4. The process for regenerating a polyester container of claim 1 , wherein the container comprises polyethylene terephthalate in an amount of 90% by weight or more.
5. The process for regenerating a polyester container of claim 1 , wherein the copolymerized polyester resin comprises neopentyl glycol in an amount of 5 to 35% by mole based on the total number of moles of the diol component and terephthalate in an amount of at least 90% by mole based on the total number of moles of the dicarboxylic acid component.
6. The process for regenerating a polyester container of claim 1 , wherein the copolymerized polyester resin comprises ethylene glycol in an amount of 55 to 93% by mole and diethylene glycol in an amount of 2 to 10% by mole based on the total number of moles of the diol component.
7. The process for regenerating a polyester container of claim 1 , wherein the heat shrinkable film has a melting point of 190° C. or higher as measured by differential scanning calorimetry.
8. The process for regenerating a polyester container of claim 1 , wherein the crystallization temperature of the heat shrinkable film is not measured or is 70° C. to 95° C. by differential scanning calorimetry.
9. The process for regenerating a polyester container of claim 1 , wherein the step of preparing the polyester container comprises covering the outer surface of the container with the heat shrinkable film; and having the heat shrinkable film shrunk, and
the heat shrinkable film has a heat shrinkage rate of 30% or more in the main shrinkage direction upon thermal treatment at a temperature of 80° C. for 10 seconds.
10. Regenerated polyester chips prepared according to the regeneration process of claim 1 .
11. The regenerated polyester chips of claim 10 , which comprise first flakes that comprise polyethylene terephthalate and second flakes that comprise the copolymerized polyester resin.
12. The regenerated polyester chips of claim 11 , which comprise 70 to 99% by weight of polyethylene terephthalate and 1 to 30% by weight of the copolymerized polyester resin based on the total weight of the regenerated polyester chips.
13. The regenerated polyester chips of claim 11 , wherein the copolymerized polyester resin comprises neopentyl glycol in an amount of 5 to 35% by mole based on the total number of moles of the diol component and terephthalate in an amount of at least 90% by mole based on the total number of moles of the dicarboxylic acid component.
14. The regenerated polyester chips of claim 11 , wherein the copolymerized polyester resin comprises ethylene glycol in an amount of 55 to 93% by mole and diethylene glycol in an amount of 2 to 10% by mole based on the total number of moles of the diol component.
15. The regenerated polyester chips of claim 10 , which have an intrinsic viscosity (IV) of 0.60 dl/g or more.