Method of printing a three-dimensional article
A three-dimensionally printed article comprises a build material and a support material, the support material comprising a hydroxypropyl methylcellulose having a DS of at least 1.0 and an MS of at least 0.6, wherein DS is the degree of substitution of methoxyl groups and MS is the molar substitution of hydroxypropoxyl groups. The support material can be removed from the build material by contacting the support material with water.
1. A method of printing a three-dimensional article comprising:
selectively depositing layers of a fluid build material to form the three-dimensional article on a substrate; and
supporting at least one of the layers of the build material with a support material, the support material comprising a hydroxypropyl methylcellulose having a DS of at least 1.0 and an MS of at least 0.6, wherein DS is the degree of substitution of methoxyl groups and MS is the molar substitution of hydroxypropoxyl groups, and at most 5 weight percent of water.
2. The method of claim 1 , wherein the layers of the build material are deposited according to an image of the three-dimensional article in a computer readable format.
3. The method of claim 2 further comprising hardening the build material.
4. The method of claim 3 further comprising removing the support material from the build material by contacting the support material with water.
5. The method of claim 1 wherein the amount of the hydroxypropyl methylcellulose is at least 50 weight percent of the total weight of the support material.
6. The method of claim 1 wherein the hydroxypropyl methylcellulose has a DS of at least 1.4.
7. The method of claim 1 wherein the hydroxypropyl methylcellulose has a DS of from 1.6 to 2.5.
8. The method of claim 1 wherein the hydroxypropyl methylcellulose has an MS of from 0.6 to 1.7.
9. The method of claim 1 wherein the build material comprises a thermoplastic material selected from the group consisting of poly(acrylonitrile-butadiene-styrene), polycarbonate, polylactic acid and polyethylene terephthalate.
10. The method of claim 1 wherein the hydroxypropyl methylcellulose has a viscosity that is up to 30 mPa·s, determined as a 2% by weight solution in water at 20° C.
11. The method of claim 1 wherein both the build material and the support material are melted in nozzle and selectively printed.
12. The method of claim 11 wherein the hydroxypropyl methylcellulose has an MS of from 0.7 to 1.3.
13. The method of claim 1 wherein the support material has at most 3 weight percent of water.
14. The method of claim 1 wherein the support material has at most 1 weight percent of water.