Multilayer heat shrinkable films

1. A multilayer heat-shrinkable film comprising a tie layer directly adhered to a surface of a barrier layer, the barrier layer comprising polyvinylidene chloride and the tie layer comprising a polymer blend comprising:

a. from 50% to 85% by weight of at least a modified ethylene/alpha-olefin copolymer;

b. from 50% to 15% by weight of at least a modified ethylene and vinyl acetate copolymer, said modified ethylene and vinyl acetate copolymer having a percentage by weight of vinyl acetate between 6% and 15%.

2. The multilayer heat-shrinkable film of claim 1 further comprising an outer heat sealable layer.

3. The multilayer heat-shrinkable film of claim 1 , wherein the barrier layer is an inner layer of the multilayer heat-shrinkable film.

4. The multilayer heat-shrinkable film of claim 1 having a total free shrink at 85° C. of at least 40%.

5. The multilayer heat-shrinkable film of claim 1 , wherein the modified ethylene/alpha-olefin copolymer comprises at least one member selected from modified heterogeneous polymer, modified homogeneous polymer, modified very low density polyethylene, and modified ultralow density polyethylene, and the modified ethylene and vinyl acetate copolymer is anhydride modified.

6. The multilayer heat-shrinkable film of claim 1 , wherein the modified ethylene/alpha-olefin copolymer is an ethylene/alpha-olefin copolymer comprising at least one anhydride functionality grafted thereon and/or copolymerized therewith and/or blended therewith.

7. The multilayer heat-shrinkable film of claim 1 , wherein the density of the modified ethylene/alpha-olefin copolymer is in the range from 0.905 g/cc to 0.927 g/cc, and/or the Melt Flow Index of the modified ethylene/alpha-olefin copolymer, measured at 190° C., 2.16 kg (ASTM 01238) is in the range from 2 to 10 g/10 min.

8. The multilayer heat-shrinkable film of claim 1 , wherein the Melt Flow Index of the modified ethylene/vinyl acetate copolymer is in the range from 2.0 to 5.5 g/10 min, measured at 190° C., 2.16 kg, as per ASTM 01238) and/or the melting point is from 87 to 100° C.

9. The multilayer heat-shrinkable film of claim 1 , wherein the polymer blend of the tie layer comprises from 65% to 75% by weight of at least a modified ethylene/alpha-olefin copolymer having a density between 0.910 and 0.920 g/cc and from 35% to 25% by weight of at least a modified ethylene/vinyl acetate copolymer having a percentage by weight of vinyl acetate between 6% and 15%.

10. The multilayer heat-shrinkable film of claim 1 having an oxygen transmission rate below 100 cm3/m2·day·atm at 23° C. and 0%, according to ASTM D-3985.

11. The multilayer heat-shrinkable film of claim 1 having a haze after shrink of lower than 40%, measured according to ASTM D1003.

12. The multilayer heat-shrinkable film of claim 1 , wherein said anhydride functionality is selected from anhydride of maleic acid, anhydride of crotonic acid, anhydride of citraconic acid, anhydride of itaconic acid and anhydride of fumaric acid.

13. The multilayer heat-shrinkable film of claim 2 comprising at least two tie layers directly adhered respectively on said first and second surface of the inner barrier layer, said tie layers containing a blend comprising 50 to 85 wt % modified ethylene/alpha-olefin copolymer and 50 to 15 wt % modified ethylene/vinyl acetate copolymer having 6 to 15 wt % vinyl acetate.

14. The multilayer heat-shrinkable film of claim 13 further comprising at least one stiff resin layer comprising a polymer selected from the group consisting of polyester, polyamide, styrene-based polymer, and blends thereof.

15. The multilayer heat-shrinkable film of claim 14 , wherein:

a. the polyester is present in the film in an amount of from 3 to 50 wt % based on total film weight, and/or,

b. the polyamide is present in the film in an amount of from 5 to 55 wt % based on total film weight, and/or

c. the film contains polyamide and/or polyester in an amount of at least 20%, based on total film weight.

16. The multilayer heat-shrinkable film of claim 14 , having the following sequence of layers:

A/C/D/C/B/C/E/D/E/D

wherein:

a. layer (A) is the first outer heat sealable layer,

b. layer (B) is the inner barrier layer comprising polyvinylidene chloride,

c. layers (C) are the tie layers containing the blend comprising 50 to 85 wt % modified ethylene/alpha-olefin copolymer and 50 to 15 wt % modified ethylene/vinyl acetate copolymer having 6 to 15 wt % vinyl acetate,

d. internal layers (D) are stiff resin layers comprising polyamide,

e. outer layer (D) is the second outer layer, outer layer (D) comprising polyester, and

f. additional layers (E) comprise modified ethylene/vinyl acetate copolymer.

17. A process for the manufacture of a multilayer heat-shrinkable film comprising the steps of:

a. Coextruding a tubular substrate comprising:

I. a heat sealable layer;

II. a barrier layer comprising polyvinylidene chloride; and

III. a tie layer directly adhered to a surface of the barrier layer, the tie layer comprising a polymer blend comprising:

i. from 50% to 85% by weight of at least a modified ethylene/alpha-olefin copolymer;

ii. from 50% to 15% by weight of at least a modified ethylene and vinyl acetate copolymer, said modified ethylene and vinyl acetate copolymer having a percentage by weight of vinyl acetate between 6% and 15%; and

b. quenching the tubular substrate.

18. The process for the manufacture of a multilayer heat-shrinkable film according to claim 17 , wherein the quenching the tubular substrate is at a temperature of from 5 to 15° C. and the process further comprising the steps of:

a. extrusion coating the substrate with any remaining layers, thus obtaining an unoriented tubular film,

b. quenching the unoriented tubular film at a temperature of from 5° C. to 30° C.,

c. heating the tubular film to a temperature which is above the Tg of all the polymeric resins composing the layers and below the melting temperature of at least one of the resins employed,

d. biaxially orienting the tubular film at orientation ratios an orientation ratio of from about 2 to about 6 in each direction, and

e. quenching the oriented tubular film in cold air, at a temperature from 4 to 30° C. 30° C., preferably from: 5 to 10° C.

19. The process for the manufacture of a multilayer heat-shrinkable film of claim 17 wherein the multilayer heat-shrinkable film has a haze after shrink of lower than 40% as measured according to ASTM D 1003.

20. The process for the manufacture of a multilayer heat-shrinkable film of claim 17 further comprising the step of packaging a product within the multilayer heat-shrinkable film.