Granted Patent B2

US 12,337,416 · App. 16/406,055 · Granted Jun 24, 2025

Inventors: Jorge Alaman Aguilar (Saragossa, ES); Miguel Angel Buñuel Magdalena (Saragossa, ES); Francisco Javier Ester Sola (Saragossa, ES); Jose Ramon Garcia Jimenez (Augsburg, DE); Jose Andres Garcia Martinez (Saragossa, ES); Pilar Perez Cabeza (Saragossa, ES); Fernando Planas Layunta (Saragossa, ES)

Assignee: BSH Hausgeräte GmbH

B23K26/362B23K26/0622B23K26/361B23K26/364B23K26/40B23K26/55B23K26/57C03C17/36C03C17/3605C03C17/3684C03C23/0025F24C15/10B23K2103/172B23K2103/50C03C2218/32C03C2218/36

Abstract

Claims (40)

1. A method for embodying a hotplate for a hob having at least one cooking zone that is visible when viewing the hob on a topside and upon which a preparation vessel can be positioned for preparing food, the method comprising:

providing the hotplate, wherein the hotplate is one of a glass hotplate and a ceramic hotplate;

forming at least one metallic layer and a further layer under the at least one metallic layer on an underside of the hotplate; and

after the forming the at least one metallic layer and the further layer, forming the at least one cooking zone on the hotplate by irradiating at least one region of the at least one metallic layer with a laser light of a laser beam directed to strike the topside of the hotplate and to radiate through the hotplate and moving the laser light with respect to the at least one region of the at least one metallic layer such that an entire layer thickness of the at least one region of the at least one metallic layer disposed between the hotplate and the further layer is completely continuously removed with each movement of the laser light so that the further layer is visible from the topside of the hotplate.

2. The method of claim 1 , wherein the further layer is a color coating.

3. The method of claim 1 , wherein the at least one metallic layer is formed directly on the underside of the hotplate, and

wherein one of the at least one metallic layer and the further layer is formed by sputtering.

4. The method of claim 1 , wherein the at least one metallic layer and the further layer under the at least one metallic layer are formed on an entire underside of the hotplate.

5. The method of claim 1 , wherein the laser light is focused on the topside of the hotplate.

6. The method of claim 1 , wherein the at least one metallic layer has a thickness of less than 130 nm.

7. The method of claim 1 , wherein the at least one metallic layer has a thickness between 20 nm and 100 nm.

8. The method of claim 1 , wherein the further layer has a thickness of less than 250 μm.

9. The method of claim 1 , wherein the further layer has a thickness between 100 μm and 200 μm.

10. The method of claim 1 , wherein the laser light is moved at a speed of 2000 mm/s.

11. The method of claim 1 , wherein the laser light is generated with a pulse frequency of 110 kHz.

12. The method of claim 1 , wherein the laser light is generated with a wavelength of 532 nm.

13. The method of claim 1 , further comprising removing the at least one region of the at least one metallic layer only after the at least one metallic layer and the further layer have completely been applied on the underside of the hotplate.

14. The method of claim 13 , wherein the at least one region of the at least one metallic layer is removed in lines, which have a line width of less than 500 μm.

15. The method of claim 13 , wherein the at least one region of the at least one metallic layer is removed in lines, which have a line width of 400 μm.

16. A method for manufacturing a hotplate for a hob having at least one cooking zone that is visible when viewing the hob on a topside and upon which a preparation vessel can be positioned for preparing food, the method consisting essentially of:

providing the hotplate, wherein the hotplate is one of a glass hotplate and a ceramic hotplate;

applying at least one metallic layer on an entire underside of the hotplate;

applying at least one dielectric color coating consecutively to an entire underside of the at least one metallic layer such that the at least one metallic layer is between the hotplate and the at least one dielectric color coating; and

after applying the at least one metallic layer and the at least one dielectric color coating, forming the at least one cooking zone on the hotplate by applying a laser light of a laser beam to at least one region of the at least one metallic layer and moving the laser light with respect to the at least one region of the at least one metallic layer such that an entire layer thickness of the at least one region of the at least one metallic layer disposed between the hotplate and the at least one dielectric color coating is completely continuously removed with each movement of the laser light so that the at least one dielectric color coating is visible from the topside of the hotplate.

17. The method of claim 16 , wherein the dielectric color coating is applied directly to the at least one metallic layer.

18. The method of claim 16 , wherein the at least one metallic layer has a thickness of less than 130 nm,

wherein the further layer has a thickness of less than 250 μm,

wherein the laser light is moved at a speed of 2000 mm/s,

wherein the laser light is generated with a pulse frequency of 110 kHz,

wherein the laser light is generated with a wavelength of 532 nm, and

wherein the at least one region of the at least one metallic layer is removed in lines, which have a line width of less than 400 μm.

19. The method of claim 18 , wherein the at least one metallic layer has a thickness between 20 nm and 100 nm, and

wherein the further layer has a thickness between 100 μm and 200 μm.

20. A method for forming a hotplate for a hob having at least one cooking zone that is visible when viewing the hob on a topside and upon which a preparation vessel can be positioned for preparing food, the method consisting essentially of:

providing the hotplate, wherein the hotplate is one of a glass hotplate and a ceramic hotplate;

applying at least one metallic layer on an entire underside of the hotplate, wherein the at least one metallic layer has a thickness of less than 130 nm;

applying at least one further layer of dielectric material consecutively to an entire underside of the at least one metallic layer such that the at least one metallic layer is between the hotplate and the further layer, wherein the further layer has a thickness of less than 250 μm;

after applying the at least one metallic layer and the further layer, forming the at least one cooking zone on the hotplate that is visible when viewing the hob on the topside by irradiating at least one region of the at least one metallic layer with a laser light of a laser beam having a pulse frequency of 110 kHz and directed to strike a topside of the hotplate and to radiate through the hotplate and moving the laser light at a speed of 2000 mm/s with respect to the at least one region of the at least one metallic layer such that an entire layer thickness of the at least one region of the at least one metallic layer disposed between the hotplate and the further layer is completely continuously removed in lines having a thickness of less than 500 μm with each movement of the laser light so that the further layer is recognized when viewing the hob on the topside.

21. The method of claim 20 , wherein the at least one metallic layer has a thickness between 20 nm and 100 nm.

22. The method of claim 20 , wherein the further layer has a thickness between 100 μm and 200 μm.