3D printing build materials and support materials comprising a phosphor
In one aspect, build materials and support materials for use with a 3D printer are described herein. Such materials include a phosphor component in combination with other components. In some embodiments, the phosphor component of a build material or support material is present in the material in an amount of 0.001-0.5 wt. % and has a peak photoluminescence (PL) emission wavelength of 430-750 nm and a photoluminescence quantum yield (QY) of 0.10-1.
1. A support material for three-dimensional printing, the support material comprising:
50-80 wt. % stearyl alcohol;
5-50 wt. % hydrogenated rosin; and
0.001-5 wt. % 2,5-thiophenediylbis(5-tert-butyl-1, 3-benzoxazole), based on the total weight of the-support material.
2. The support material of claim 1 , wherein the phase change wax component comprises a hydrocarbon wax, a fatty alcohol wax, a fatty acid wax, a fatty acid ester wax, an aldehyde wax, an amide wax, a ketone wax, or a mixture or combination thereof.
3. The support material of claim 1 , wherein the phase change wax component is present in the support material in an amount of 60-75 wt. %, based on the total weight of the support material.
4. The support material of claim 1 , wherein the tackifier component comprises a rosin ester, a rosin alcohol, or a mixture or combination thereof.
5. The support material of claim 1 , wherein the tackifier component is present in the support material in an amount of 25-45 wt. %, based on the total weight of the support material.
6. The support material of claim 1 , wherein the phosphor component has a peak photoluminescence emission wavelength of 430-750 nm.
7. The support material of claim 1 , wherein the phosphor component has a photoluminescence quantum yield of 0.10-1.
8. The support material of claim 1 , wherein the phosphor component has a peak photoluminescence emission wavelength of 500-700 nm and a photoluminescence quantum yield of 0.30-1.
9. The support material of claim 1 , wherein the phosphor component is present in the support material in an amount of 0.001-0.5 wt. %, based on the total weight of the support material.