Medical protective clothing materials
Protective clothing materials and related methods and garments are provided. In some embodiments, a protective clothing material may comprise a fibrous layer that serves as a barrier to certain fluids (e.g., bodily fluids, water) and microbes. The impermeability of the fibrous layer may be due, at least in part, to the structural uniformity and/or relatively small pore size of the fibrous layer. In some embodiments, the fibrous layer may have a relatively high air permeability that imparts beneficial properties (e.g., relatively high air flow, breathability) to the protective clothing material without adversely affecting its protection rating. In certain embodiments, the protective clothing material may also comprise one or more coarse nonwoven webs that impart beneficial properties (e.g., splash resistance) to the protective clothing material. The protective clothing materials, described herein, may be particularly useful for a wide variety of applications, including the formation of AAMI level 4 protective garments.
1. A protective garment comprising:
an electrospun fibrous layer comprising synthetic fibers;
a first coarse fiber layer comprising fibers having an average fiber diameter of greater than or equal to about 10 microns; and
a second coarse fiber layer comprising fibers having an average fiber diameter of greater than or equal to about 10 microns,
wherein the electrospun fibrous layer is positioned between the coarse fiber layers.
2. The protective garment of claim 1 , wherein a mean flow pore size of the electrospun fibrous layer is greater than or equal to about 1 micron and less than or equal to about 6 microns, a maximum pore size of the electrospun fibrous layer is greater than or equal to about 4 micron and less than or equal to about 12 microns and a difference between the maximum pore size and the mean pore size is less than or equal to about 6 microns, wherein the mean flow pore size and the maximum flow pore size are determined according to the standard ASTM F316-03 (2011).
3. The protective garment of claim 1 , wherein an air permeability of the electrospun fibrous layer is greater than or equal to about 4 CFM and less than or equal to about 10 CFM.
4. The protective garment of claim 1 , wherein the protective garment is configured as a surgical apparel or a surgical drape.
5. The protective garment of claim 1 , wherein the average diameter of the synthetic fibers of the electrospun fibrous layer is greater than or equal to about 0.01 microns and less than or equal to about 0.05 microns.
6. The protective garment of claim 1 , wherein the mean flow pore size of the electrospun fibrous layer is greater than or equal to about 2 microns and less than or equal to about 5 microns, wherein the mean flow pore size is determined according to the standard ASTM F316-03 (2011).
7. The protective garment of claim 1 , wherein the maximum pore size of the electrospun fibrous layer is greater than or equal to about 6 microns and less than or equal to about 9 microns, wherein the maximum flow pore size is determined according to the standard ASTM F316-03 (2011).
8. The protective garment of claim 1 , wherein the electrospun fibrous layer is less than or equal to about 6 mils.
9. The protective garment of claim 1 , wherein the electrospun fibrous layer has a basis weight of less than or equal to about 50 g/m2.
10. The protective garment of claim 1 , wherein the electrospun fibrous layer may have a moisture vapor transmission rate of greater than or equal to about 100 g/m2 day.
11. The protective garment of claim 1 , wherein a standard deviation of an air permeability of the electrospun fibrous layer is greater than or equal to about 0 CFM and less than or equal to about 1 CFM.