The present disclosure relates to polyamide compositions and resulting injection-molded articles that can be plated, e.g., metal coated, to form structurally aesthetic injection-molded articles. The polyamide compositions may include from 40 wt. % to 80 wt. % of a polyamide, from 0.5 wt. % to 40 wt. % of an etchable filler, from 5 wt. % to 30 wt. % of glass fiber, optionally less than 40 wt. % of a semi-structural mineral, and optionally from 0.1 wt. % to 13 wt. % of additive. The polyamide composition imparts very good surface appearance and excellent mechanical properties to injection-molded articles that are substantially free of visual defects.
1. A polyamide composition comprising:
from 40 wt. % to 80 wt. % of a polyamide comprising a copolymer or terpolymer comprising 6,6, 6I, and 6 units;
from 1 wt. % to 26 wt. % of a surface treated etchable filler comprising magnesium hydroxide treated with a silane;
from 5 wt. % to 30 wt. % of glass fibers having an average diameter up to 9.5 microns;
less than 40 wt. % of a semi-structural mineral; and
from 0.1 wt. % to 13 wt. % of additive comprising inorganic stabilizers, organic stabilizers, flame retardants, lubricants, dyes, pigments, nucleating agents, metal flakes, impact modifiers, antistatic agents, conductivity additives, mold-release agents, optical brighteners, adhesion promoters, ageing inhibitors, antioxidants, antiozonants, light stabilizers, UV stabilizers, UV absorbers, UV blockers, inorganic heat stabilizers, organic heat stabilizers, processing aids, crystallization accelerators, crystallization retarders, flow aids, or particulate fillers, or combinations thereof.
2. The composition of claim 1 , wherein the polyamide is a copolymer comprising PA-6,6 and PA-6I, wherein the PA-6I ranges from 2 wt. % to 20 wt. %.
3. The composition of claim 1 , wherein the polyamide is a terpolymer comprising PA-6,6, PA-6, and PA-6I, wherein the terpolymer comprises PA-6I ranging from 2 wt. % to 20 wt. % and PA-6 ranging from 2 wt. % to 20 wt. %.
4. The composition of claim 1 , wherein the additive comprises from 1 wt. % to 10 wt. % of pigment, from 0.05 wt. % to 1 wt. % of lubricant, and/or from 0.25 wt. % to 2 wt. % of processing aid, wherein the pigment comprises a thermally stable nigrosine, wherein the lubricant comprises zinc stearate, and wherein the processing aid comprises a substituted piperidine compound.
5. The composition of claim 1 , wherein the glass fibers have an average diameter ranging from 4 microns to 8 microns.
6. The composition of claim 1 , wherein the composition comprises a semi-structural mineral, wherein the semi-structural mineral comprises one or more of kaolin, mica, talc, and wollastonite.
7. The composition of claim 1 , wherein the composition has a distinctness of image greater than 50 as measured by Byk Gardner Wave Scan meter, and wherein the composition has a R-value greater than 5 as measured by Byk Gardner Wave Scan meter.
8. The composition of claim 1 , wherein the composition has a density ranging from 1.25 g/cm 3 to 1.6 g/cm 3 , and wherein the composition has a melting point ranging from 220° C. to 260° C.
9. The composition of claim 1 , wherein the polyamide is a copolymer comprising PA-6,6 and PA-6I, wherein the composition includes glass fibers having an average diameter ranging from 4 microns to 8 microns, wherein the composition has a density ranging from 1.3 g/cm 3 to 1.6 g/cm 3 , wherein the composition has a distinctness of image greater than 65 as measured by Byk Gardner Wave Scan meter, wherein the composition has a R-value greater than 7 as measured by Byk Gardner Wave Scan meter.
10. The composition of claim 1 , wherein the polyamide is a terpolymer comprising PA-6,6, PA-6I, and PA-6, wherein the composition includes glass fibers having an average diameter ranging from 4 microns to 8 microns, wherein the composition has a density ranging from 1.3 g/cm 3 to 1.6 g/cm 3 , wherein the composition has a distinctness of image greater than 65 as measured by Byk Gardner Wave Scan meter, wherein the composition has a R-value greater than 7 as measured by Byk Gardner Wave Scan meter.
11. An injection-molded article formed from the composition of claim 1 , wherein the injection-molded article is plated with a metal comprising one or more of copper, manganese, tin, nickel, iron, chrome, zinc, gold, platinum, cobalt, phosphorus, aluminum, and alloys thereof.
12. A polyamide composition comprising:
from 40 wt. % to 80 wt. % of a polyamide comprising a copolymer or terpolymer comprising 6,6, 6I, and 6 units;
from 1 wt. % to 26 wt. % of a silane-coated magnesium hydroxide;
from 5 wt. % to 30 wt. % of glass fiber having an average diameter up to 9.5 microns;
less than 40 wt. % of kaolin; and
from 0.1 wt. % to 13 wt. % of additive comprising inorganic stabilizers, organic stabilizers, flame retardants, lubricants, dyes, pigments, nucleating agents, metal flakes, impact modifiers, antistatic agents, conductivity additives, mold-release agents, optical brighteners, adhesion promoters, ageing inhibitors, antioxidants, antiozonants, light stabilizers, UV stabilizers, UV absorbers, UV blockers, inorganic heat stabilizers, organic heat stabilizers, processing aids, crystallization accelerators, crystallization retarders, flow aids, or particulate fillers, or combinations thereof.
13. The composition of claim 12 , wherein the additive comprises from 0.5 wt. % to 10 wt. % of thermally stable nigrosine, from 0.05 wt. % to 1 wt. % of zinc stearate, and/or from 0.25 wt. % to 2 wt. % of substituted piperidine compound.
14. A process for preparing an injection-molded article comprising:
providing a polyamide composition comprising:
from 40 wt. % to 80 wt. % of a polyamide comprising a copolymer or terpolymer comprising 6,6, 6I, and 6 units;
from 1 wt. % to 26 wt. % of a surface treated etchable filler comprising magnesium hydroxide treated with a silane;
from 5 wt. % to 30 wt. % of glass fiber having an average diameter up to 9.5 microns;
less than 40 wt. % of a semi-structural mineral; and
from 0.1 wt. % to 13 wt. % of additive comprising inorganic stabilizers, organic stabilizers, flame retardants, lubricants, dyes, pigments, nucleating agents, metal flakes, impact modifiers, antistatic agents, conductivity additives, mold-release agents, optical brighteners, adhesion promoters, ageing inhibitors, antioxidants, antiozonants, light stabilizers, UV stabilizers, UV absorbers, UV blockers, inorganic heat stabilizers, organic heat stabilizers, processing aids, crystallization accelerators, crystallization retarders, flow aids, or particulate fillers, or combinations thereof;
heating the polyamide composition;
filling a mold cavity with the heated polyamide composition;
cooling the heated polyamide composition to form the injection-molded article.
15. The process of claim 14 , further comprising etching a surface of the injection-molded article with an etching solution, wherein the etching solution does not comprise any hexavalent chromium.
16. The process of claim 14 , further comprising plating the etched surface of the injection-molded article with a metal comprising one or more of copper, manganese, tin, nickel, iron, chrome, zinc, gold, platinum, cobalt, phosphorus, aluminum, and alloys thereof.