Alpha-alumina flakes
A blended composition containing uncoated Al 2 O 3 flakes having a thickness of ≥500 nm and a D 50 -value of 15-30 μm and a D 90 -value of 30-45 μm, and/or coated Al 2 O 3 flakes having a thickness of ≥500 nm and a D 50 -value of 15-30 μm and a D 90 -value of 30-45 μm, which have been coated with at least one layer of a metal oxide, mixtures of at least two metal oxides, metal, metal sulphide, titanium suboxide, titanium oxynitride, FeO(OH), metal alloys and/or rare earth compounds, and their use in various formulations.
1. A blended composition, comprising a first and a second components, which are blended together, wherein the first component is: coated Al 2 O 3 flakes having a thickness of ≥500 nm and a D 50 -value of 15-30 μm and a D 90 -value of 30-45 μm and a D 10 -value of ≤9.0 μm, which have been coated with a coating selected from the group consisting of at least one layer of a metal oxide, mixtures of at least two metal oxides, metal, metal sulphide, titanium suboxide, titanium oxynitride, FeO(OH), metal alloys and rare earth compounds, and wherein the second component is: one or more of organic dyes, organic pigments, pigments, transparent pigments, opaque white pigments, colored pigments, black pigments, flake-form iron oxides, organic pigments, holographic pigments, liquid crystal polymers, transparent luster pigments, colored luster pigments, black luster pigments based on metal oxide-coated mica, SiO 2 flakes, fillers, natural mica, synthetic mica, nylon powder, pure melamine resins, filled melamine resins, talc, SiO 2 , glasses, kaolin, oxides of aluminum, oxides of magnesium, oxides of calcium, oxides of zinc, hydroxides of aluminum, hydroxides of magnesium, hydroxides of calcium, hydroxides of zinc, BiOCl, barium sulfate, calcium sulfate, calcium carbonate, magnesium carbonate, carbon, and physical or chemical combinations thereof, wherein the coated Al 2 O 3 flakes are α-alumina flakes.
2. The blended composition according to claim 1 , wherein the coated Al 2 O 3 flakes have a D 10 -value of 9.0 μm.
3. The blended composition according to claim 1 , wherein the coated Al 2 O 3 flakes have a D 90 -value of 30-40 μm.
4. The blended composition according to claim 1 , wherein the coated Al 2 O 3 flakes have a particle thickness of 550-1000 nm.
5. The blended composition according to claim 1 , wherein the coated Al 2 O 3 flakes have been doped with a dopant selected from the group consisting of TiO 2 , ZrO 2 , SiO 2 , SnO 2 , In 2 O 3 , ZnO and combinations thereof.
6. The blended composition according to claim 5 , wherein the amount of doping is 0.01-5% by weight based on the total weight of the Al 2 O 3 flake.
7. The blended composition according to claim 5 , wherein the coated Al 2 O 3 flakes have been doped with TiO 2 .
8. The blended composition according to claim 1 , which contain the Al 2 O 3 flakes coated with a coating selected from the group consisting of at least one layer of a metal oxide, mixtures of at least two metal oxides, metal, metal sulphide, titanium suboxide, titanium oxynitride, FeO(OH), metal alloys and rare earth compounds.
9. The blended composition according to claim 1 , wherein the Al 2 O 3 flakes have been coated with at least one layer of a metal oxide or a mixture of at least two metal oxides.
10. The blended composition according to claim 1 , wherein the Al 2 O 3 flakes have been coated with the following layer sequence:
Al 2 O 3 flake+TiO 2
Al 2 O 3 flake+TiO 2 /Fe 2 O 3
Al 2 O 3 flake+Fe 2 O 3
Al 2 O 3 flake+TiO 2 +Fe 2 O 3
Al 2 O 3 flake+TiO 2 +Fe 3 O 4
Al 2 O 3 flake+TiO 2 +SiO 2 +TiO 2
Al 2 O 3 flake+Fe 2 O 3 +SiO 2 +TiO 2
Al 2 O 3 flake+TiO 2 /Fe 2 O 3 +SiO 2 +TiO 2
Al 2 O 3 flake+TiO 2 +SiO 2 +TiO 2 /Fe 2 O 3
Al 2 O 3 flake+TiO 2 +SiO 2
Al 2 O 3 flake+TiO 2 +SiO 2 /Al 2 O 3
Al 2 O 3 flake+TiO 2 +Al 2 O 3
Al 2 O 3 flake+SnO 2
Al 2 O 3 flake+SnO 2 +TiO 2
Al 2 O 3 flake+SnO 2 +Fe 2 O 3
Al 2 O 3 flake+SiO 2
Al 2 O 3 flake+SiO 2 +TiO 2
Al 2 O 3 flake+SiO 2 +TiO 2 /Fe 2 O 3
Al 2 O 3 flake+SiO 2 +Fe 2 O 3
Al 2 O 3 flake+SiO 2 +TiO 2 +Fe 2 O 3
Al 2 O 3 flake+SiO 2 +TiO 2 +Fe 3 O 4
Al 2 O 3 flake+SiO 2 +TiO 2 +SiO 2 +TiO 2
Al 2 O 3 flake+SiO 2 +Fe 2 O 3 +SiO 2 +TiO 2
Al 2 O 3 flake+SiO 2 +TiO 2 /Fe 2 O 3 +SiO 2 +TiO 2
Al 2 O 3 flake+SiO 2 +TiO 2 +SiO 2 +TiO 2 /Fe 2 O 3
Al 2 O 3 flake+SiO 2 +TiO 2 +SiO 2
Al 2 O 3 flake+SiO 2 +TiO 2 +SiO 2 /Al 2 O 3
Al 2 O 3 flake+SiO 2 +TiO 2 +Al 2 O 3
Al 2 O 3 flake+TiO 2 +Prussian Blue or
Al 2 O 3 flake+TiO 2 +Carmine Red.
11. The blended composition according to claim 1 , wherein the Al 2 O 3 flakes have been coated with TiO 2 in the rutile or anatase modification.
12. The blended composition according to claim 1 , wherein the Al 2 O 3 flakes have been coated with TiO 2 in the rutile modification.
13. The blended composition according to claim 1 , wherein the coated Al 2 O 3 flakes consist of 40-90 wt. % of Al 2 O 3 flakes and 10-60 wt. % of the coating based on the total weight of the Al 2 O 3 flake.
14. The blended composition according to claim 1 , wherein the coated Al 2 O 3 flakes have a D 10 -value of <9.0 μm.
15. The blended composition according to claim 1 , consisting of a first and a second components, which are blended together, wherein the first component is: coated Al 2 O 3 flakes having a thickness of ≥500 nm and a D 50 -value of 15-30 μm and a D 90 -value of 30-45 μm and a D 10 -value of ≤9.0 μm, which have been coated with a coating selected from the group consisting of at least one layer of a metal oxide, mixtures of at least two metal oxides, metal, metal sulphide, titanium suboxide, titanium oxynitride, FeO(OH), metal alloys and rare earth compounds, and wherein the second component is: one or more of organic dyes, organic pigments, pigments, transparent pigments, opaque white pigments, colored pigments, black pigments, flake-form iron oxides, organic pigments, holographic pigments, liquid crystal polymers, transparent luster pigments, colored luster pigments, black luster pigments based on metal oxide-coated mica, SiO 2 flakes, fillers, natural mica, synthetic mica, nylon powder, pure melamine resins, filled melamine resins, talc, SiO 2 , glasses, kaolin, oxides of aluminum, oxides of magnesium, oxides of calcium, oxides of zinc, hydroxides of aluminum, hydroxides of magnesium, hydroxides of calcium, hydroxides of zinc, BiOCl, barium sulfate, calcium sulfate, calcium carbonate, magnesium carbonate, carbon, and physical or chemical combinations thereof.
16. The blended composition according to claim 1 , wherein the coated Al 2 O 3 flakes have a particle thickness of 550-1000 nm.
17. A formulations from the areas of paints, coatings, automobile coatings, automotive finishing, industrial coatings, paints, powder coatings, printing inks, security printing inks, plastics, ceramic materials, cosmetics, glasses, paper, paper coating, toners for electrophotographic printing processes, seeds, greenhouse sheeting and tarpaulins, thermally conductive, self-supporting, electrically insulating, flexible sheets for the insulation of machines or devices, as absorber in the laser marking of paper and plastics, absorber in the laser welding of plastics, pigment pastes with water, organic and/or aqueous solvents, in pigment preparations and dry preparations, which comprises the blended composition according to claim 1 .
18. A formulation comprising 0.01-95% by weight the blended composition according to claim 1 , based on the formulation as a whole.
19. A formulation comprising the blended composition according to claim 1 and at least one component selected from the group consisting of water, polyols, polar and nonpolar oils, fats, waxes, film formers, polymers, copolymers, surfactants, free-radical scavengers, antioxidants, stabilisers, odour enhancers, silicone oils, emulsifiers, solvents, preservatives, thickeners, rheological additives, fragrances, colorants, effect pigments, UV absorbers, surface-active assistants and/or cosmetic active compounds, fillers, binders, pearlescent pigments, color pigments and organic dyes.