Catalysts, systems, and methods for the conversion of biomass to chemicals
The present disclosure relates to a composition that includes a solid support, a metal positioned on the solid support, and an oxide coating positioned to at least partially cover the metal. The compositions described herein may be utilized in methods that include contacting muconic acid and hydrogen to convert at least a portion of the muconic acid to adipic acid.
1. A composition comprising:
a solid support;
a metal positioned on the solid support; and
an oxide coating positioned to at least partially cover the metal; and
wherein:
the metal comprises palladium,
the solid support comprises at least one of titanium dioxide or alumina,
the oxide coating comprises between one oxide coating and five oxide coatings of at least one of titanium dioxide or alumina,
each oxide coating has a thickness between 1 nm and 5 nm,
the metal has an accessibility between 85% and 95% as measured by carbon monoxide chemisorption,
the metal is present at a concentration between 0.1 wt % and 1 wt % relative to the metal and the solid support, and
the solid support is in the form of a cylinder having a characteristic length between 0.5 mm and 5 mm and a surface area between 25 m 2 /g and 200 m 2 /g as measured by nitrogen physisorption.
2. The composition of claim 1 , wherein the solid support has a first characteristic length between 1 micron and 10 mm.
3. The composition of claim 1 , wherein the metal comprises at least one of ruthenium, rhodium, palladium, silver, osmium, iridium, platinum, or gold.
4. The composition of claim 1 , wherein the metal is present at a concentration between 0.1 wt % and 2.4% and at a concentration between 2.6% and 5.0 wt % relative to the metal and the solid support.
5. The composition of claim 1 , wherein the metal is in the form of a particle having a second characteristic length of less than one micron.
6. The composition of claim 1 , wherein the oxide coating comprises at least one of silica, titanium oxide, cerium oxide, magnesium oxide, tin oxide, or nickel oxide.
7. The composition of claim 1 , wherein the oxide coating has a thickness between 0.4 nm and 100 nm.
8. The composition of claim 1 , wherein the oxide coating comprises at least one of a crack or a pore.
9. A method comprising:
contacting muconic acid and hydrogen with a catalyst comprising:
a solid support;
a metal positioned on the solid support; and
an oxide coating positioned to at least partially cover the metal,
wherein:
the metal comprises palladium,
the solid support comprises at least one of titanium dioxide or alumina,
the oxide coating comprises between one oxide coating and five oxide coatings of at least one of titanium dioxide or alumina,
each oxide coating has a thickness between 1 nm and 5 nm,
the metal has an accessibility between 85% and 95% as measured by carbon monoxide chemisorption,
the metal is present at a concentration between 0.1 wt % and 1 wt % relative to the metal and the solid support, and
the solid support is in the form of a cylinder having a characteristic length between 0.5 mm and 5 mm and a surface area between 25 m 2 /g and 200 m 2 /g as measured by nitrogen physisorption,
wherein:
the contacting is performed with the muconic acid in a liquid phase comprising an alcohol, and
the contacting converts at least a portion of the muconic acid to adipic acid.
10. The method of claim 9 , wherein the alcohol comprises ethanol.
11. The method of claim 9 , wherein the hydrogen is supplied at a pressure between 1 atmosphere and 100 atmosphere.
12. The method of claim 9 , wherein the contacting is performed in a stirred tank reactor.
13. The method of claim 9 , wherein the contacting is performed at a temperature between 20° C. and 100° C.
14. The method of claim 9 , wherein the contacting is performed in a packed-bed reactor.