Method for producing electrode for aluminum electrolytic capacitor
Provided is a method for producing an electrode for an electrolytic capacitor, the method comprising: a hydration step in which an aluminum electrode is immersed in a hydration treatment solution having a temperature of 80° C. or higher; and a chemical conversion step in which the aluminum electrode is subjected to chemical conversion treatment up to a formation voltage of at least 400 V. The hydration treatment solution contains a hydration inhibitor. The thickness of a hydrated film formed in the hydration step satisfies the following condition, 0.6≤t2/t1≤1, wherein t1 is the average thickness of the hydrated film formed in a depth range of up to 100 μm from the surface of the aluminum electrode, and t2 is the average thickness s of the hydrated film formed in a deep portion at least 100 μm from the surface of the aluminum electrode.
1. A method for producing an electrode for an aluminum electrolytic capacitor, the method comprising:
a hydration step of forming a hydrated film onto an aluminum electrode including a porous layer having a thickness of 200 μm to 50000 μm per layer on an aluminum core part by immersing the aluminum electrode into a hydration treatment liquid including a hydration inhibiting agent and having a temperature of 80° C. or more; and
a chemical formation step of performing chemical formation of the aluminum electrode to a chemical formation voltage of 400 V or more after the hydration step, wherein
the thickness of the hydrated film formed in the hydration step satisfies the following conditions:
0.6≤ t 2/ t 1≤1
where an average thickness of the hydrated film formed in a range from the surface of the aluminum electrode to a depth of 100 μm is t1 and an average thickness of the hydrated film formed in a deep part having a depth of 100 μm or more from the surface of the aluminum electrode is t2,
wherein the hydration inhibiting agent is a sugar having a carbon number of 3 or more or a sugar alcohol having a carbon number of 3 or more.
2. The method for producing the electrode for the aluminum electrolytic capacitor according to claim 1 , wherein the hydration treatment liquid has a pH of 5.0 to 9.0.
3. The method for producing the electrode for the aluminum electrolytic capacitor according to claim 1 , wherein the hydration inhibiting agent is any one of ribulose, xylulose, ribose, arabinose, xylose, lyxose, deoxyribose, psicose, fructose, sorbose, tagatose, allose, altrose, glucose, mannose, gulose, idose, galactose, talose, fucose, fuculose, rhamnose, sedoheptulose, mannitol, sorbitol, xylitol, sucrose, lactulose, lactose, maltose, trehalose, cellobiose, lactitol, maltitol, nigerose, raffinose, maltotriose, melezitose, stachyose, acarbose, and amylose.
4. The method for producing an electrode for an aluminum electrolytic capacitor according to claim 1 , wherein the porous layer is made of sintered layers of aluminum powder, and the aluminum electrode is formed by laminating the porous layer onto aluminum core material as the core part.
5. The method for producing an electrode for an aluminum electrolytic capacitor according to claim 1 , wherein the chemical formation step includes first chemical formation treatment for subjecting the aluminum electrode to chemical formation in an aqueous solution including an organic acid or a salt thereof and second chemical formation treatment for subjecting the aluminum electrode to chemical formation in an aqueous solution including an inorganic acid or a salt thereof after the first chemical formation treatment.