Polypropylene composition for foaming applications
The present invention is directed to a polypropylene composition (C) comprising a heterophasic propylene copolymer and an inorganic filler, the use of said polypropylene composition (C) for the production of a foamed article and a foamed article obtained from said polypropylene composition (C).
1. A polypropylene composition (C), comprising:
a) at least 20 wt. %, based on the overall weight of the polypropylene composition (C), of a heterophasic propylene copolymer (HECO1) comprising:
i) a matrix (M) comprising a first propylene polymer (PP1), and
ii) an elastomeric propylene copolymer (E),
b) at least 30 wt. %, based on the overall weight of the polypropylene composition (C), of a second propylene polymer (PP2),
c) a propylene homopolymer (H-PP3) having a melt flow rate MFR 2 (230° C.) determined according to ISO 1133 below 50 g/10 min,
d) an adhesion promoter (AP), and
e) an inorganic filler (F),
wherein said first propylene polymer (PP1) and said second propylene polymer (PP2) have melt flow rates MFR 2 (230° C.) determined according to ISO 1133 above 50 g/10 min.
2. The polypropylene composition (C) according to claim 1 , wherein the heterophasic propylene copolymer (HECO1) has a melt flow rate MFR 2 (230° C.) determined according to ISO 1133 in the range of 10 to 30 g/10 min.
3. The polypropylene composition (C) according to claim 2 , comprising:
a) 20 to 40 wt. % of the heterophasic propylene copolymer (HECO1) comprising the first propylene copolymer (PP1) and the elastomeric propylene copolymer (E),
b) 30 to 55 wt. % of the second propylene polymer (PP2),
c) 5 to 25 wt. % of the propylene homopolymer (H-PP3),
d) 0.5 to 5 wt. % of the adhesion promoter (AP), and
e) 10 to 30 wt. % of the inorganic filler (F),
based on the overall weight of the polypropylene composition (C).
4. The polypropylene composition (C) according to claim 1 , wherein the inorganic filler (F) is glass fibers.
5. The polypropylene composition (C) according to claim 1 , wherein the adhesion promoter (AP) is a polar modified polypropylene (PM-PP) being a propylene homo- or copolymer grafted with maleic anhydride having a melt flow rate MFR (190° C.) determined according to ISO 1133 of at least 50 g/10 min.
6. The polypropylene composition (C) according to claim 1 , wherein the heterophasic propylene copolymer (HECO1) has:
i) a comonomer content in the range of 5.0 to 35.0 mol %, and/or
ii) a xylene soluble fraction (XCS) in the range of 15.0 to 40.0 wt. %,
based on the overall weight of the heterophasic propylene copolymer (HECO1).
7. The polypropylene composition (C) according to claim 1 , wherein the heterophasic propylene copolymer (HECO1) has an intrinsic viscosity of the xylene soluble fraction (XCS) measured according to ISO 1628/1 (at 135° C. in decalin) in the range of 1.0 to 4.5 dl/g.
8. The polypropylene composition (C) according to claim 1 , wherein the first propylene polymer (PP1) and/or the second propylene polymer (PP2) are propylene homopolymers.
9. The polypropylene composition (C) according to claim 1 , wherein the elastomeric propylene copolymer (E) is a copolymer of propylene and ethylene.
10. The polypropylene composition (C) according to claim 1 , having a melt flow rate MFR 2 (230° C.) determined according to ISO 1133 in the range of 8 to 30 g/10 min.
11. The polypropylene composition (C) according to claim 1 , wherein said polypropylene composition (C) is a foamable polypropylene composition.
12. A foamed article, comprising the polypropylene composition (C) according to claim 1 .
13. The foamed article according to claim 12 , wherein said foamed article is an automotive article.