Hot dip coated steel having excellent processability
Disclosed are a hot dip coated steel and a method for manufacturing the same, the hot dip coated steel comprising a hot rolled steel and a hot dip coated layer formed on the surface of the hot rolled steel, wherein the hot rolled steel comprises: by wt %, 0.05-0.15% of C, 0.5% or less of Si (excluding 0%), 0.5-1.5% of Mn, 0.01-0.05% of Nb, 0.005-0.05% of V, 0.03% or less of P (excluding 0%), 0.015% of S or less (excluding 0%), 0.05% or less of Al (excluding 0%), 0.01% or less of N (excluding 0%), and the balance of Fe and inevitable impurities; 90 area % or more of ferrite as the microstructure thereof; and 5,000-15,000/μm 2 of V-based precipitates.
1. A hot dip coated steel, comprising a hot rolled steel and a hot dip coated layer formed on a surface of the hot rolled steel,
wherein the hot rolled steel includes 0.05 wt % to 0.15 wt % of carbon (C), 0.5 wt % or less of silicon (Si) (excluding 0 wt %), 0.5 wt % to 1.5 wt % of manganese (Mn), 0.01 wt % to 0.05 wt % of niobium (Nb), 0.005 wt % to 0.05 wt % of vanadium (V), 0.03 wt % or less of phosphorous (P) (excluding 0 wt %), 0.015 wt % or less of sulfur (S) (excluding 0 wt %), 0.05 wt % or less of aluminum (Al) (excluding 0 wt %), 0.01 wt % or less of nitrogen (N) (excluding 0%), and the balance of iron (Fe) and inevitable impurities, includes 90 area % or more of ferrite as the microstructure thereof, and includes 5,000 to 15,000/μm 2 of V-based precipitates.
2. The hot dip coated steel of claim 1 , wherein an average diameter of the V-based precipitates is 5 nm to 10 nm.
3. The hot dip coated steel of claim 1 , wherein a maximum diameter of the V-based precipitates is 20 nm or less.
4. The hot dip coated steel of claim 1 , wherein an aspect ratio of the ferrite is 0.8 to 1.4.
5. The hot dip coated steel of claim 1 , wherein the balance other than the ferrite is at least one of pearlite and bainite.
6. The hot dip coated steel of claim 1 , wherein the inevitable impurities includes chromium (Cr), nickel (Ni), molybdenum (Mo), and copper (Cu), and are suppressed to 0.05 wt % or less (excluding 0%) of Cr, 0.05 wt % or less (excluding 0%) of Ni, 0.01 wt % or less (excluding 0%) of Mo, and 0.01 wt % or less (excluding 0%) of Cu.
7. The hot dip coated steel of claim 1 , wherein the hot dip coated layer includes at least one of zinc (Zn), Al, and magnesium (Mg).
8. The hot dip coated steel of claim 1 , wherein the product of yield strength and elongation is 12,000 MPa % to 15,000 MPa %.