Hot-dip galvanized steel plate with excellent bake hardenability and anti-aging property at room temperature
Provided is a hot-dip galvanized steel plate which is applicable as a material for a vehicle outer panel and has an excellent bake hardenability and anti-aging property at room temperature, and a method for manufacturing a hot-dip galvanized steel plate, the method comprising a process including the steps of: winding a hot-rolled steel plate, followed by cooling at a speed of 0.002-0.027° C./sec; cold-rolling the cooled steel plate; continuously annealing the cold-rolled steel plate; and cooling the annealed steel plate in the multi-stage manner of primary to third rounds.
1. A hot-dip galvanized steel sheet comprising:
a cold-rolled steel sheet; and
a hot-dip galvanized layer formed on the cold-rolled steel sheet,
wherein the cold-rolled steel sheet comprises, by weight %, 0.005 to 0.08% of C, 1.3 to 2.3% of Mn, 1.0% or less of Cr excluding 0%, 0.1% or less of P excluding 0%, 0.01% or less of S excluding 0%, 0.01% or less of N excluding 0%, 0.01 to 0.06% of sol.Al, one or more of 0.3% or less of Si, 0.2% or less of Mo and 0.003% or less of B, and a balance of Fe and inevitable impurities,
wherein ferrite and martensite are included as a microstructure of the cold-rolled steel sheet, and
wherein, K, an average concentration ratio of solid solution carbon before and after baking determined by Expression 1 below, is 0.2 to 0.7,
K=C 1 /C 2 [Expression 1]
where C 1 and C 2 are an average concentration of solid solution C before and after baking performed for 20 minutes at 140° C., respectively, in an area within 100 nm in a direction of a ferrite grain from a grain boundary of ferrite and martensite at a t/4 position (t=a thickness of the cold-rolled sheet) from a surface of the cold-rolled steel sheet.
2. The hot-dip galvanized steel sheet of claim 1 , wherein the cold the microstructure comprises: 90 to 99 area % of the ferrite and 1 to 10 area % of the martensite.
3. The hot-dip galvanized steel sheet of claim 1 , wherein the microstructure further comprises bainite, and an area ratio of bainite, B, defined by Expression 2 below, is 3 or less,
B={A B /(A F +A M +A B )}×100 [Expression 2]
where A F indicates an area ratio of ferrite, A M indicates an area ratio of martensite, and A B is an area ratio of bainite.
4. The hot-dip galvanized steel sheet of claim 1 , wherein the cold-rolled steel sheet satisfies Relational Expression 1 below,
0.001≤[Mn]/150+[Cr]/100+[Mo]/90≤0.026 [Relational Expression 1]
where Mn, Cr, and Mo indicate a content of each element by weight %.
5. The hot-dip galvanized steel sheet of claim 1 , wherein the hot-dip galvanized layer comprises: one or more elements selected from the group consisting of Si, Al, and Mg.
6. The hot-dip galvanized steel sheet of claim 1 , wherein, after the baking, an amount of bake hardenability, BH, is 35 MPa or higher, and when a heat treatment is performed for 1 hour at 100° C., an yield point, YP-El, is 0.2% or less, including 0%.