Multilayer composite material and method for manufacturing

1. A multilayer composite comprising:

a first monolayer comprising parallel ultrahigh molecular weight polyethylene (UHMWPE) fibers aligned in a first fiber direction and at least one first matrix material; and

a layer of leather having a thickness of between 0.5-6 mm in contact with the first monolayer, wherein

fibers are present in the first monolayer in an amount to provide a fiber density of between 2-30 grams per square meter, and wherein

the at least one first matrix material has a stiffness of at most 2 MPa.

2. The multilayer composite of claim 1 further comprising:

a second monolayer in contact with the first monolayer, wherein

the second monolayer comprises parallel fibers aligned in a second fiber direction and a second matrix material, and wherein

the first monolayer is rotated relative to the second monolayer in the multilayer composite such that the second fiber direction is offset relative to the first fiber direction by up to 90 degrees.

3. The multilayer composite of claim 2 , further comprising:

additional monolayers of parallel fibers, wherein each of the additional monolayers comprise parallel fibers and a matrix, wherein

the additional monolayers are stacked and arranged in the multilayer composite such that one monolayer of the additional monolayers is in contact with the second monolayer, and wherein each successive monolayer of the additional monolayers is rotated relative to an adjacent monolayer such that fiber directions are offset in each successive monolayer.

4. The multilayer composite of claim 3 , further comprising a polymeric film in contact with a monolayer such as to form an outer layer of the composite.

5. The multilayer composite of claim 4 , wherein the polymeric film is waterproof/breathable.

6. The multilayer composite of claim 1 , wherein the strength of the UHMWPE fibers is at least 0.5 GPa.

7. The multilayer composite of claim 1 , wherein the strength of the UHMWPE fibers is at least 2.5 GPa.

8. The multilayer composite of claim 1 , wherein the UHMWPE fibers have an intrinsic viscosity of at least 5 dl/g.

9. The multilayer composite of claim 1 , wherein the at least one first matrix material is at least one selected from the group consisting of polyacrylates, polymers functionalized with acrylate groups, and polyurethanes.

10. The multilayer composite of claim 3 , wherein the UHMWPE fibers are present in the second monolayer and any one of the additional monolayers at a fiber density of between 1 and 50 grams per square meter.

11. A process for manufacturing a multilayer composite comprising:

(a) providing an assembly comprising:

(i) a layer of leather having a thickness between 0.5-6 mm in contact with a removable cover which includes a pattern for embossing or texturizing the leather surface,

(ii) at least one monolayer comprising parallel aligned fibers and a matrix material, and

(iii) optionally at least one polymeric film layer, wherein

the assembly has two outer surfaces, wherein one of the outer surfaces is the layer of leather in contact with the removable cover; and

(b) compressing the assembly at a pressure between 1 and 5 bar and a temperature between 35 and 120° C.

12. An article which comprises the multilayer composite of claim 1 , wherein the article is selected from the group consisting of footwear, sports apparel, clothing, luggage, leather goods for animals, bags and luggage, hats, jackets, wallets, purses, bags, upholstery and gloves.