Wire rod with excellent strength and ductility and manufacturing method therefor
Disclosed are a wire rod and a manufacturing method therefor, the wire rod comprising, by weight %: 0.05-0.20% of C, 0.2% or less of Si, 5.0-6.0% of Mn, 0.020% or less of P, 0.020% or less of S, 0.010-0.050% of Al, 0.010-0.020% of N, and a balance of Fe and inevitable impurities and having a microcrystalline structure composed of two phases of austenite and ferrite, wherein the austenite has an area fraction of 15-25%.
1. A wire rod, by weight %, comprising:
0.05 to 0.20% of carbon (C), 0.2% or less of silicon (Si), 5.0 to 6.0% of manganese (Mn), 0.020% or less of phosphorus (P), 0.020% or less of sulfur (S), 0.010 to 0.050% of aluminum (Al), 0.010 to 0.020% of nitrogen (N), a balance of iron (Fe) and inevitable impurities, and having a microstructure composed of two phases of austenite and ferrite,
wherein an area fraction of austenite is 15 to 25%,
wherein the microstructure of the wire rod has a lamellar structure of austenite and ferrite in a form of a lath,
wherein an inter-lamellar spacing is 0.2 μm or less, excluding 0 μm, and
wherein the following Relational Expression 2 is satisfied,
1≤[Al]/[N]≤4 [Relational Expression 2]
where, each of [Al] and [N] means a content (by weight %) of the corresponding element.
2. The wire rod of claim 1 , wherein the following Relational Expression 1 is satisfied,
[Mn]/[Si]≥25 [Relational Expression 1]
(where, each of [Mn] and [Si] means a content (by weight %) of the corresponding element).
3. The wire rod of claim 1 , wherein a dislocation density formed inside the lath is 1.0×10 15 m −2 or more.
4. The wire rod of claim 1 , wherein the wire rod comprises aluminum nitride (AlN), and a maximum circle equivalent diameter of the AlN is 30 nm or less, excluding 0 nm.
5. The wire rod of claim 1 , wherein a tensile strength is 1200 to 1400 MPa and elongation is 30% or more.