Method for producing lithium hydroxide from lithium phosphate
The present invention relates to a method of manufacturing lithium hydroxide, which includes adding at least one acid selected from hydrochloric acid, sulfuric acid, and nitric acid into lithium phosphate slurry including a lithium phosphate particle, adding an alkali material to the lithium phosphate slurry including the acid, and converting it into a lithium hydroxide aqueous solution.
1. A method of manufacturing lithium hydroxide, comprising
adding at least one acid selected from hydrochloric acid, sulfuric acid, and nitric acid into lithium phosphate slurry including a lithium phosphate particle;
adding an alkali material to the lithium phosphate slurry including the acid and converting it into a lithium hydroxide aqueous solution; and
after adding the alkali material to the lithium phosphate slurry including the acid and converting it into the lithium hydroxide aqueous solution, concentrating the lithium hydroxide aqueous solution to prepare the lithium hydroxide,
wherein an amount of the added acid ranges from 0.67 equivalents to 1.0 equivalents based on an amount of the lithium phosphate particle, and
the lithium phosphate slurry including the acid has a lithium concentration of 4,000 mg/L to 2,000 mg/L.
2. The method of manufacturing lithium hydroxide of claim 1 , wherein an amount of the added alkali material may range from 0.8 to 1.5 equivalents based on an amount of the lithium phosphate particle.
3. The method of manufacturing lithium hydroxide of claim 1 , wherein the alkali material is one or more selected from the group consisting of Ca(OH) 2 , NaOH, and CaO.
4. The method of manufacturing lithium hydroxide of claim 1 , wherein in the step of adding the alkali material to the lithium phosphate slurry including the acid and converting it into the lithium hydroxide aqueous solution, gypsum and hydroxyapatite are precipitated.