Aluminum material for fluxfree CAB brazing
An aluminum alloy brazing sheet has a 3XXX, 1XXX or 6XXX core, an interliner and a 4XXX brazing layer without added Mg. The interliner has Bi and Mg, the magnesium migrating to the surface of the brazing sheet during brazing and reducing the aluminum oxide to facilitate brazing without flux in a controlled inert atmosphere with reduced oxygen.
1. A sheet material for fluxfree CAB brazing, the sheet material comprising:
a core layer comprised of 3XXX, 1XXX or 6XXX series aluminum alloy;
an interliner layer comprised of 0.25 to 1.7 wt % Mg, 0.3-0.95 wt % Si, 0.09-0.5 wt % Bi, and aluminum; and
a brazing liner layer comprised of 4XXX aluminum alloy, wherein the interliner layer is disposed between the core layer and the brazing liner layer, and the core layer, the interliner layer and the brazing liner layer are conjoined together forming the sheet material.
2. The sheet material of claim 1 , wherein the interliner layer further comprises up to 1.8 wt % Mn, up to 0.9 wt % Cu, up to 0.7 wt % Fe, up to 0.18 wt % Ti, up to 3.0 wt % Zn, up to 0.25 wt % Cr, and up to 0.15 wt % Zr.
3. The sheet material of claim 1 , wherein the brazing liner layer has a composition of Mg<0.05wt %.
4. The sheet material of claim 1 , wherein the brazing liner layer has a composition of Bi<0.010 wt %.
5. The sheet material of claim 1 , wherein the core layer comprises 0.08-1.1 wt % Si, 0.15 to 0.7 wt % Fe, 0.05-1.0 wt % Cu, 0.4-1.8 wt % Mn, up to 0.5 wt % Mg, up to 2 wt % Zn, up to 0.25 wt % Cr, and up to 0.15 wt % Zr.
6. The sheet material of claim 1 , wherein the brazing liner layer comprises 5-12 wt % Si, up to 0.7 wt % Fe, up to 3 wt % Zn, aluminum and incidental impurities.
7. The sheet material of claim 1 , wherein the core layer comprises from 60% to 90% of a total thickness of the sheet material, the interliner layer comprises from 3% to 20% of the total thickness and the brazing liner layer comprises from 3% to 20% of the total thickness.
8. The sheet material of claim 1 , wherein the interliner layer is a first interliner layer and further comprising a second interliner layer having a composition like that of the first interliner layer, the second interliner layer being disposed on the core layer opposite to the first interliner layer.
9. The sheet material of claim 8 , wherein the brazing liner layer is a first brazing liner layer and further comprising a second brazing liner layer disposed over the second interliner layer distal to the core layer.
10. The sheet material of claim 1 further comprising an additional aluminum alloy layer disposed on the core layer opposite the interliner layer, wherein the additional aluminum alloy layer is comprised of at least one alloy selected from the group consisting of a 3XXX alloy, a 3XXX+Zn alloy, a 1XXX alloy, a 7XXX alloy and a 4XXX alloy.
11. The sheet material of claim 1 , wherein the sheet material is formed into a first part and further comprising a second part made from aluminum alloy, the first part and the second part joined together by a brazed joint at least partially formed from the brazing liner layer of the first part.
12. The sheet material of claim 11 , wherein the sheet material is a portion of a heat exchanger such as an oil cooler or radiator.
13. The sheet material of claim 12 , wherein the heat exchanger has an internal hollow devoid of flux residue.
14. The sheet material of claim 1 , wherein the Mg present in the interliner layer is from 0.25 to 0.95 wt %.
15. The sheet material of claim 1 , wherein the Mg present in the interliner layer is from 1.0 to 1.7 wt %.
16. The sheet material of claim 1 , wherein the Si present in the interliner layer is from 0.3 to 0.65 wt %.
17. The sheet material of claim 1 , wherein the Si present in the interliner layer is from 0.7 to 0.95 wt %.
18. The sheet material of claim 1 , wherein the Bi present in the interliner layer is from 0.09 to 0.24 wt %.
19. The sheet material of claim 1 , wherein the Bi present in the interliner layer is from 0.25 to 0.50 wt %.