Aluminum-based alloy plated steel sheet having excellent processing part corrosion resistance
Provided is an aluminum-based alloy plate steel sheet, which comprises a base steel sheet, an interfacial alloy layer, and an aluminum-based plated layer comprising a Mg—Si-based alloy phase, and in which b/a is 1-5 when the area fraction of the Mg—Si-based alloy phase contained in the aluminum-based plated layer is a and the area fraction of the Mg—Si-based alloy phase contained in the region of the lower 20% in the thickness direction of the aluminum-based plated layer is b.
1. An aluminum-based alloy plated steel sheet, comprising:
a base steel sheet;
an interfacial alloy layer; and
an aluminum-based plated layer comprising a magnesium-silicon (Mg—Si)-based alloy phase,
wherein b/a is 1 to 5 when an area ratio of the Mg—Si based alloy phase contained in the aluminum-based plated layer is a and an area ratio of a Mg—Si based alloy phase contained in a region of a lower 20% of the aluminum-based plated layer in a thickness direction is b.
2. The aluminum-based alloy plated steel sheet of claim 1 , wherein at least a portion of the Mg—Si based alloy phase is in contact with the interfacial alloy layer, and in Mg—Si based alloy phases in contact with the interfacial alloy layer, when a sum of lengths of the Mg—Si based alloy phases projected through an interface between the base steel sheet and the interfacial alloy layer is c and a length of an interface between the base steel sheet and the interfacial alloy layer is d, c/d is 0.2 to 0.8.
3. The aluminum-based alloy plated steel sheet of claim 2 , wherein an average hardness of the Mg—Si based alloy phases in contact with the interfacial alloy layer is 400 to 600 Hv.
4. The aluminum-based alloy plated steel sheet of claim 2 , wherein in the Mg—Si based alloy phases in contact with the interfacial alloy layer, when an average of lengths of the Mg—Si based alloy phases projected through an interface between the base steel sheet and the interfacial alloy layer is e and an average height of the Mg—Si based alloy phases in contact with the interfacial alloy layer is f, f/e is 0.2 to 3.
5. The aluminum-based alloy plated steel sheet of claim 2 , wherein when an average interval of the Mg—Si based alloy phases in contact with the interfacial alloy layer is g and an average thickness of the aluminum-based plated layer is t, Equation 1: t/5≤g≤t is satisfied.
6. The aluminum-based alloy plated steel sheet of claim 1 , wherein the base steel sheet comprises 5 to 35 wt % of Mn.
7. The aluminum-based alloy plated steel sheet of claim 1 , wherein the interfacial alloy layer comprises, by weight %, 40 to 70% of aluminum (Al), 3 to 10% of manganese (Mn), 2 to 13% of silicon (Si), a remainder of iron (Fe), and unavoidable impurities.
8. The aluminum-based alloy plated steel sheet of claim 1 , wherein the interfacial alloy layer has a thickness of 0.1 to 10 μm.
9. The aluminum-based alloy plated steel sheet of claim 1 , wherein the aluminum-based plated layer comprises, by weight %, 3 to 15% of silicon (Si), 0.1 to 10% of magnesium (Mg), a remainder of aluminum (Al), and unavoidable impurities.
10. The aluminum-based alloy plated steel sheet of claim 9 , wherein the aluminum-based plated layer further comprises, by weight %, one or more of 0.001 to 5% of calcium (Ca), 0.005 to 2% of strontium (Sr), 0.01 to 2% of manganese (Mn), 0.01 to 2% of chromium (Cr), 0.01 to 2% of molybdenum (Mo), and 0.1 to 10% of tin (Sn).