Multilayer non-cross-linked heat-shrinkable packaging films
The present invention provides a multilayer packaging film characterized by an improved sealability even through contamination with excellent shrinkability good optics and strength without using internal layers of stiff resins and cross-linking, to flexible containers made therefrom, such as bags, pouches and the like, useful for packaging articles, in particular food items.
1. A multilayer heat-shrinkable non-cross-linked packaging film comprising at least:
an outer sealant layer (a),
an outer polyester layer (b),
an inner gas barrier layer (c),
a first core layer (d1) positioned between the outer sealant layer (a) and the inner gas barrier layer (c),
a second core layer (d2) positioned between the inner gas barrier layer (c) and the outer polyester layer (b), and
no inner layer comprising a major proportion of polyamide(s) or polyester(s), characterized in that
the core layers (d1) and (d2) do not comprise a major proportion of tie resins,
the percentage ratio of the total thickness of the first core layer (d1) and the second core layer (d2) in respect of the total thickness of the film (r1) is from 35% to 60%,
the percentage ratio of the thickness of the outer polyester layer (b) in respect of the total thickness of the film (r3) is from 3% to 15%, and
the core layer(s) (d1) and/or (d2) independently comprise a major proportion of (I) a blend (B) of a polyethylene component (e1) not having a bimodal molecular weight distribution and of a second resin (R) selected from ethylene-vinyl acetate copolymer(s) (R1), acrylic acid copolymer(s) (R2), acrylate copolymer(s) (R3) and their admixtures,
wherein said polyethylene component (e1) is present in amount of at least 40% by weight and said second resin (R) is present in an amount of from 10% to 60% by weight in respect of the blend (B) weight, and the ratio of the thickness of the first core layer (d1) in respect of the second core layer (d2) (r2) is from 0.4 to 2.2; or
(II) a polyethylene component (e2) having a bimodal molecular weight distribution, wherein
said polyethylene component (e2) has a density from 0.900 g/cc to 0.910 g/cc, and the ratio of the thickness of the first core layer (d1) in respect of the second core layer (d2) (r2) is from 0.4 to 2.2.
2. The film according to claim 1 wherein said polyethylene component (e1) has a density from 0.895 g/cc to 0.915 g/cc.
3. The film according to claim 1 wherein the percentage ratio of the thickness of the outer polyester layer (b) in respect of the total thickness of the film (r3) is from 5% to 10%.
4. The film according to claim 1 wherein said outer polyester layer (b), comprises more than 70% by weight of aromatic polyester(s) in respect of outer polyester layer (b) weight.
5. The film according to claim 1 wherein the polyester(s) of the outer polyester layer (b) have an intrinsic viscosity (IV) not higher than 0.80 MPa·sec measured according to ASTM D4603-03 and/or a melting point higher than the melting point of the polymer(s) in the outer sealant layer (a).
6. The film according to claim 1 wherein the polyester(s) of the outer polyester layer (b) is an aromatic polyester selected from poly(ethylene 2,6-naphtalate), poly(butylene terephthalate), poly(ethylene terephthalate), copolyesters obtained by reacting one or more aromatic dicarboxylic acids with one or more dihydroxy alcohols, (such as PETG) and their admixtures.
7. The film according to claim 1 wherein the inner gas barrier layer (c) comprises polyvinylidene chloride (PVDC), or the inner gas barrier layer (c) comprises of PVDC.
8. The film according to claim 1 wherein the core layers (d1) and (d2) have the same composition.
9. The film according to claim 1 wherein the core layers (d1) and (d2) independently consists of
the blend (B) or
the polyethylene component (e2) having a bimodal molecular weight distribution or
the polyethylene component (e2) in admixture with said second resin (R), wherein said second resin (R) is present in amount up to 50% by weight in respect of the corresponding core layers (d1) or (d2) weight.
10. The film according to claim 1 wherein the blend (B) comprises from 50% to 90% by weight of said polyethylene component (e1) and/or at least 10% of said second resin (R) with respect to the blend (B) weight.
11. The film according to claim 1 wherein the core layers (d1) and (d2) do not include more than 30%.
12. The film according to claim 1 wherein the total thickness of the film is from 10 to 150 microns.
13. The film according to claim 1 wherein:
(r1) is from 35% to 55%, and/or
(r2) is from 0.6 to 2.1.
14. The film according to claim 1 , wherein said film has a total free shrink at 85° C. measured according to ASTM D2732 higher than 80%.
15. The film according to claim 1 , wherein said film has a value of haze (%) after shrink at 85° C. in water measured according to ASTM D1003 not higher than 25.