Adhesive coating composition for non-oriented electrical steel sheet, and method for manufacturing non-oriented electrical steel sheet
The present invention has been made in an effort to provide an adhesive coating composition capable of adhering (fastening) a non-oriented electrical steel sheet without using a conventional fastening method such as welding, clamping, or interlocking, a non-oriented electrical steel sheet stack to which the same is applied, and a manufacturing method thereof. According to an exemplary embodiment of the present invention, an adhesive coating composition includes: 40 to 99 wt % of a first component containing a water-soluble resin; and 1 to 60 wt % of a second component containing a composite metal phosphate.
1. An adhesive coating composition for a non-oriented electrical steel sheet, the composition consisting of:
40 to 99 wt % of a water-soluble resin; and
1 to 60 wt % of a composite metal phosphate,
wherein the water-soluble resin has an aromatic functional group and is at least one selected from an epoxy-based resin, a siloxane-based resin, an acrylic-based resin, a phenol-based resin, a styrene-based resin, a vinyl-based resin, an ethylene-based resin, and a urethane-based resin, and
the composite metal phosphate is at least one selected from a primary aluminum phosphate (Al(H 3 PO 4 ) 3 ), a primary cobalt phosphate (Co(H 3 PO 4 ) 2 ), a primary calcium phosphate (Ca(H 3 PO 4 ) 2 ), a primary zinc phosphate (Zn(H 3 PO 4 ) 2 ), and a primary magnesium phosphate (Mg(H 3 PO 4 ) 2 ).
2. The adhesive coating composition of claim 1 , wherein
the water-soluble resin includes at least one functional group selected from benzene, toluene, xylene, naphthalene, anthracene, and benzopyrene.
3. The adhesive coating composition of claim 1 , wherein
a solid content of the water-soluble resin is 50 wt %, and the water-soluble resin has a weight average molecular weight of 1000 to 100,000 and glass transition temperature (Tg) of 30 to 150° C.