Heat-treated PVC-plastic panel
The present invention relates to a method of treating PVC plates as well as plates and panels manufactured by this method. Further, the invention relates to plates and panels, in particular wall, ceiling or floor panels, comprising a heat-treated carrier plate ( 12 ) based on polyvinyl chloride with a density of, for example, 900 to 2,500 kg/m 3 and a film ( 17 ) applied thereon. The film is a thin PVC-film and comprises a decorative pattern ( 18 ) directly printed thereon.
1. A method of treating a polyvinyl chloride (PVC) plate comprising the following steps in the given order:
providing a PVC plate;
heating the PVC plate in an oven to at least 70° C.;
cooling the heated plate.
2. The method according to claim 1 , wherein the plate is heated to at least its glass transition temperature.
3. The method according to claim 1 , wherein the plate is kept at the minimum temperature for at least 3 minutes.
4. The method according to claim 1 , wherein the plate is heated with a heating gradient of 2° C./min to 20° C./min on average.
5. The method according to claim 1 , wherein the plate is cooled down in a controlled manner, in a cooling oven, with a cooling gradient of 3° C./min to 20° C./min on average.
6. The method according to claim 5 , wherein the PVC plate is fed through the oven on a conveyor and the oven is a continuous oven, and the cooling of the heated plate occurs in the continuous oven.
7. The method according to claim 1 , wherein the PVC plate is provided with a PVC film having a thickness of 0.04 to 0.2 mm before or after the heat treatment.
8. A panel, comprising a polyvinyl chloride plate and a film attached thereto, wherein the film is a PVC film having a thickness of 0.04 to 0.2 mm and comprising a decorative pattern directly printed thereon, and a cured polymer layer is provided over the PVC film, and wherein the polyvinyl chloride plate contains no plasticizers.
9. The panel according to claim 8 , wherein the polymer layer comprises a hardness gradient, so that the hardness of the polymer layer decreases essentially continuously with increasing depth as seen from the surface of the polymer layer.
10. The panel according to claim 8 , wherein the printing ink used for printing the decorative pattern ( 18 ) is solvent based and a UV printing ink, and contains a polymerizable acrylate and/or N-vinylcaprolactam.
11. The panel according to claim 8 , wherein the PVC film has a thickness from 0.05 to 0.15 mm.
12. The panel according to claim 8 , wherein the PVC plate comprises a thickness between 3 and 20 mm.
13. The panel according to claim 8 , wherein a layer comprising a UV primer is provided on the PVC film.
14. The panel according to claim 8 , wherein the PVC film is glued or thermally welded to the plate.
15. A method for manufacturing of a panel, comprising the following steps:
performing a method according to claim 1 , wherein a PVC film having a thickness of 0.04 to 0.2 mm is applied to the PVC plate before or after the heat treatment;
printing a decorative pattern directly on the PVC film;
applying at least a first polymer layer to the PVC film; and
curing the polymer layer.
16. The method according to claim 15 , wherein a heated calender is used for applying the PVC film in such a way that the PVC film is thermally welded to the carrier plate.
17. The method according to claim 15 , wherein the decorative pattern is directly printed on the PVC film by means of digital printing.
18. The method according to claim 15 , wherein the PVC film has a thickness of 0.05 to 0.15 mm.
19. The panel according to claim 8 , wherein the polyvinyl chloride plate consists of PVC-U.