Polyurethane Adhesive-Backed Roofing Membranes and Methods of Making the Same
The present disclosure relates to a reverse transfer method of forming a multi-layered roofing membrane composite that includes a release liner, a polyurethane pressure sensitive adhesive layer, and a single-ply roofing membrane. The disclosed methods include coating either a release liner or a single ply membrane with the pressure sensitive adhesive layer to form a composite roll for transport.
1 .- 15 . (canceled)
16 . A process for forming a self-adhering roofing membrane composite, the process comprising:
coating a pressure sensitive adhesive layer on a release liner to form an adhesive-release liner composite;
contacting the pressure sensitive adhesive layer to a single ply membrane; and
applying pressure to the adhesive-release liner composite and the single ply membrane to form a self-adhering roofing membrane composite.
17 . The process of claim 16 , wherein the release liner comprises paper, film, or a combination thereof; and is silicone coated.
18 . The process of claim 16 , wherein the pressure sensitive adhesive layer comprises a polyurethane adhesive derived from an isocyanate prepolymer component and a resin component.
19 . The process of claim 18 , wherein the polyurethane adhesive has an isocyanate index of about 0.60 to about 0.95.
20 . The process of claim 16 , wherein the single-ply membrane comprises ethylene propylene diene monomer, thermoplastic material, modified bitumen material, or a combination thereof.
21 . The process of claim 16 , wherein the release liner is a film comprising polyethylene, polypropylene, polyester, or a combination thereof.
22 . The process of claim 16 , wherein the pressure sensitive adhesive layer defines a thickness of about 0.005 inches to about 0.50 inches.
23 . The process of claim 16 , wherein the pressure sensitive adhesive layer is prepared from a two-part adhesive composition that includes a first component comprising an isocyanate prepolymer having from about 8 to about 10% NCO content, and a second component comprising a polyol and a catalyst.
24 . The process of claim 16 , wherein the pressure sensitive adhesive layer has adequate dead load performance at a temperature from about 49° C. (about 120° F.) to about 82° C. (about 180° F.).
25 . The process of claim 16 , further comprising unwinding the adhesive-release liner composite from a first roll, and unwinding the single ply membrane from a second roll before contacting the pressure sensitive adhesive layer to the single ply membrane.
26 . The process of claim 16 , wherein the singly-ply membrane requires no pre-treatment before contacting the pressure sensitive adhesive layer to the single ply membrane.
27 . A pressure sensitive adhesive composition for use in roofing applications, the pressure sensitive adhesive composition comprising:
a first component comprising an isocyanate prepolymer having about 8 to about 10% NCO content; and
a second component comprising a polyol and a catalyst.
28 . The pressure sensitive adhesive composition of claim 27 , wherein the second component includes from about 0.5 to about 1.0 weight % of tertiary amine catalyst, from about 1.0 to about 3.0 weight % of low molecular weight diol, from about 95 to about 98 weight % of about 6,000 molecular weight triol, and from about 0.1 to about 1.0 weight % water.
29 . A process for forming a self-adhering roofing membrane composite, the process comprising:
coating a pressure sensitive adhesive layer on a single-ply membrane to form an self-adhering roofing membrane; and
contacting the pressure sensitive adhesive layer to release liner to form a self-adhering roofing membrane composite.
30 . The method of claim 29 , wherein the single-ply membrane comprises ethylene propylene diene monomer, thermoplastic material, modified bitumen material, or a combination thereof.
31 . The method of claim 29 , wherein the release liner comprises paper, film, or a combination thereof; and the release liner is silicone coated.
32 . The method of claim 29 , wherein the pressure sensitive adhesive layer has adequate dead load performance at a temperature from about 49° C. (about 120° F.) to about 82° C. (about 180° F.).
33 . The method of claim 29 , wherein the singly-ply membrane requires no pre-treatment before coating the first side of the pressure sensitive adhesive layer to the single-ply membrane.
34 . The method of claim 29 , wherein the pressure sensitive adhesive layer is a polyurethane adhesive derived from a two part adhesive composition having an isocyanate prepolymer component and a resin component.
35 . The method of claim 34 , wherein the polyurethane adhesive has an isocyanate index of about 0.60 to about 0.95.