Method and composition for improved agglomeration resistance of polyamide polymers
The present disclosure provides a leaching process and resulting composition which prevents or substantially reduces agglomeration of polyamide 6/66 copolymers. The leaching process includes applying hot water in the presence of an agglomeration inhibitor to the polyamide 6/66 copolymers in order to separate unreacted caprolactam and small molecular weight oligomers from the copolymers while preventing or substantially reducing agglomeration of the copolymers.
1. A method of improving agglomeration resistance of a polyamide polymer comprising the steps of:
polymerizing at least one polyamide copolymer from caprolactam monomers and adipic acid and hexamethylenediamine monomers, the at least one polyamide copolymer including between 80 mol % and 99 mol % caprolactam monomers and between 1 mol % and 20 mol % of combined adipic acid and hexamethylenediamine monomers, based on the total moles of caprolactam monomers and adipic acid and hexamethylenediamine monomers; and
leaching the at least one polyamide copolymer with a solution of water in the presence of an agglomeration inhibitor comprising stearic acid at a temperature between 80° C. and 140° C.
2. The method of claim 1 , wherein the amount of agglomeration inhibitor used in the leaching step is between 0.05 wt. % and 2 wt. %, based on the total solids weight of the copolymer.
3. The method of claim 1 , wherein the at least one polyamide copolymer includes between 80 mol % and 85 mol % caprolactam monomers and between 15 mol % and 20 mol % adipic acid and hexamethylenediamine monomers, based on the total moles of caprolactam monomers and adipic acid and hexamethylenediamine monomers.
4. A method of improving agglomeration resistance of a polyamide polymer, comprising the steps of:
forming at least one polyamide copolymer polymerized from caprolactam monomers and adipic acid and hexamethylenediamine monomers, the at least one polyamide copolymer including between 80 mol % and 99 mol % caprolactam monomers and between 1 mol % and 20 mol % of combined adipic acid and hexamethylenediamine monomers, based on the total moles of caprolactam monomers and adipic acid and hexamethylenediamine monomers, the at least one polyamide copolymer having an initial concentration of acid/amine terminal ends; and
leaching the at least one polyamide copolymer with a solution of water in the presence of an agglomeration inhibitor comprising stearic acid to reduce the initial concentration of acid/amine terminal ends by 5% to 25%.
5. The method of claim 4 , wherein the leaching step is carried out at a temperature between 80° C. and 140° C.