Process for the synthesis, with multiple seeding, of zeolite crystals having a controlled particle size
The present invention relates to a process for preparing zeolite crystals having a multimodal particle size distribution, and the sizes of which are between 0.02 μm and 20 μm, said process comprising a first introduction of one or more seeding agents into the tubular reactor or upstream of the tubular reactor, and at least one second introduction of one or more, identical or different, seeding agents into the tubular reactor.
1. Process for preparing zeolite crystals having a multimodal particle size distribution, and the sizes of which are between 0.02 μm and 20 μm, said process comprising at least the following steps:
a) preparing a synthesis gel by mixing at least one source of silica, at least one source of alumina and optionally, at least one aqueous alkali or alkaline-earth metal hydroxide solution,
b) feeding a tubular reactor with said synthesis gel,
c) first introduction of one or more seeding agents into the tubular reactor or upstream of the tubular reactor,
d) second introduction of one or more, identical or different, seeding agents into the tubular reactor,
e) carrying out the crystallization reaction, in the tubular reactor, of the synthesis gel in the presence of the seeding agent(s), forming the reaction medium,
f) filtering the reaction medium in order to recover crystals produced.
2. Process according to claim 1 , wherein step d) is repeated one, two, three or more times.
3. Process according to claim 1 , wherein the first introduction of seeding agent(s) is carried out upstream of the reactor.
4. Process according to claim 1 , wherein the seeding agent is chosen from nucleating gels, zeolite crystals, mineral particles, and mixtures thereof.
5. Process according to claim 1 , wherein the crystallization reaction is carried out at a temperature of between 60° C. and 200° C.
6. Process according to claim 1 , wherein the crystallization reaction is carried out at a pressure between atmospheric pressure and 1.5 MPa.
7. Process according to claim 1 , wherein a supplement of synthesis gel is added to the reaction medium, at one or more points of the tubular reactor.
8. Process according to claim 1 , wherein the total amount of seeding agent(s) added represents between 0.005% and 10% by weight relative to the synthesis gel introduced at the start into the tubular reactor.
9. Process according to claim 1 , wherein the mother liquors from the filtration step f) are recycled.
10. Process according to claim 1 , wherein the zeolite crystals are crystals of zeolite chosen from zeolites of MFI type, zeolites of MOR type, zeolites of OFF type, zeolites of MAZ type, zeolites of CHA type, zeolites of HEU type, zeolites of FAU type, zeolites of EMT type, and zeolites of the LTA type.