Three dimensional shaped article
The invention relates to a three dimensional shaped article having an outer and inner surface, the outer surface comprising at least one fabric ( 100 ) of polyethylene fibers having a tensile strength of at least 1.5 GPa, the fabric is impregnated with an acrylic based thermoplastic material. The three dimensional shaped article may further comprise monolayers with unidirectional aligned fibers. The three dimensionally shaped article has an improved surface appearance which would therefore need little or no post treatment and has good adhesion to coatings and paints.
1. A three-dimensional shaped article having an outer and inner surface, wherein the outer surface comprises:
at least one fabric of polyethylene multifilament yarns having a tensile strength of at least 1.5 GPa, wherein
the at least one fabric is a woven fabric or a knitted network, and wherein
the fabric is impregnated with an acrylic based thermoplastic material having a glass transition temperature of at least 25° C.
2. The article according to claim 1 , wherein the acrylic based thermoplastic material has a glass transition temperature of at least 35° C.
3. The article according to claim 1 , wherein the acrylic based thermoplastic material is present in an amount between 4 and 35 wt %.
4. The article according to claim 1 , wherein the yarns are ultrahigh molecular weight polyethylene (UHMWPE) yarns.
5. The article according to claim 1 , wherein the fabric is a plain woven fabric.
6. The article according to claim 1 , further comprising at least one layer of unidirectionally aligned ultra-high molecular weight polyethylene (UHMWPE) fibers.
7. The article according to claim 1 , further comprising at least two layers of unidirectionally aligned ultra-high molecular weight polyethylene (UHMWPE) fibers.
8. The article according to claim 6 , wherein the at least one monolayer of unidirectional aligned fibers comprises a matrix material having a 100% modulus of at least 3 MPa.
9. The article according to claim 8 , wherein the matrix material is a thermoplastic polyurethane.
10. The article according to claim 1 , wherein the article has an areal weight between 75 and 1250 gram per square meter.
11. The article according to claim 1 , wherein the article has an areal weight between 125 and 1000 gram per square meter.
12. The article of claim 1 , wherein the article is a helmet.
13. The article of claim 1 , wherein the article is radome.
14. The article according to claim 7 , wherein each of the two monolayers of unidirectionally aligned fibers comprises a matrix material having a 100% modulus of at least 3 MPa.
15. The article according to claim 14 , wherein the matrix material is a thermoplastic polyurethane.
16. A process for the manufacture of the three-dimensional shaped article according to claim 1 having an outer and inner surface, wherein the process comprises the steps of:
(a) providing the at least one fabric forms the outer layer of the article, wherein the at least one fabric is a woven fabric or a knitted network formed of polyethylene multifilament yarns having a tensile strength of at least 1.5 GPa which is impregnated with an acrylic based thermoplastic material having a glass transition temperature of at least 25° C., and
(b) forming a stack by stacking the at least one fabric provided according to step (a) with at least one optional layer of unidirectional aligned fibers,
(c) providing a mold for shaping the three dimensional article,
(d) optionally coating the mold surface with a mold release agent,
(e) positioning the stack formed according to step (b) in the mold, followed by
(f) compressing the stack positioned in the mold at a temperature between 90 and 135° C., at a pressure between 1 and 35 MPa, during a time of between 2 and 60 minutes to form a compressed stack, followed by
(g) cooling the compressed stack to a temperature below 80° C. to thereby provide the three-dimensional shaped article, and releasing the obtained three-dimensional shaped article from the mold.