Styrenic copolymer blend with low shrinkage
The invention relates to polymer blends of a styrene copolymer A selected from the group consisting of styrene acrylonitrile copolymers (SAN), styrene acrylonitrile maleic anhydride terpolymers (SMA), styrene acrylic copolymers, acrylonitrile butadiene styrene terpolymers (ABS), acrylonitrile butadiene styrene terpolymers with polyamide (ABS/PA), and acrylonitrile styrene acrylate terpolymers (ASA); and at least one copolymer B selected from the group consisting of styrene-butadiene block copolymers (SBC) and styrene-isoprene block copolymers (SIS); wherein the mold shrinkage of the polymer blend is reduced by at least 5% compared to the mold shrinkage of the pure styrene copolymer A.A process for the preparation of the polymer blends and the uses of the polymer blends in an injection molding process are described.
1. A polymer blend with at least two different copolymer components, comprising:
(a) 89.0 to 99.5 wt.-% of at least one styrene copolymer A selected from the group consisting of styrene acrylonitrile maleic anhydride terpolymers (SMA) with the relative composition of 20 to 30 wt.-% acrylonitrile, 0.5 to 3 wt.-% maleic anhydride, and 67 to 79.5 wt.-% styrene;
(b) 0.5 to 4.5 wt.-% of at least one copolymer B selected from the group consisting of styrene-butadiene block copolymers (SBC) and styrene-isoprene block copolymers (SIS); and
(c) 0 to 5.0 wt.-% of at least one additive C;
wherein the wt.-% refers to the complete polymer blend,
and wherein the mold shrinkage of the polymer blend is reduced by at least 5% compared to the
mold shrinkage of the pure styrene copolymer A.
2. The polymer blend according to claim 1 , wherein the mold shrinkage of the styrene copolymer A is in the range
from 0.3 to 0.7 for the styrene acrylonitrile maleic anhydride copolymer (SMA).
3. The polymer blend according to claim 1 , comprising:
(i) 89.0 to 99.0 wt.-% of at least one styrene copolymer A, and
(ii) 1.0 to 4.5 wt.-% of at least one copolymer B.
4. The polymer blend according to claim 1 , wherein the copolymer B is a styrene-butadiene block copolymer (SBC).
5. The polymer blend according to claim 1 , wherein the copolymer B is a styrene-isoprene block copolymer (SIS).
6. The polymer blend according to claim 1 , wherein the mold shrinkage of the polymer blend is reduced by at least 10% as compared to the mold shrinkage of the styrene copolymer A component.
7. A process for the preparation of the polymer blend according to claim 1 , comprising the steps of mixing component A, B, and optionally C.
8. The process according to claim 7 , wherein a mixture of components A and B, and optionally component C are extruded in an extruder at a temperature above 100° C. to give the polymer blend.
9. A method of use of a polymer blend according to claim 1 in an injection molding process.
10. A polymer article produced by injection molding of a polymer blend, which blend comprises:
(a) 89.0 to 99.5 wt.-% of at least one styrene copolymer A selected from the group consisting of styrene acrylonitrile maleic anhydride terpolymers (SMA) with the relative composition of 20 to 30 wt.-% acrylonitrile, 0.5 to 3 wt.-% maleic anhydride, and 67 to 79.5 wt.-% styrene
(b) 0.5 to 4.5 wt.-% of at least one copolymer B selected from the group consisting of styrene-butadiene block copolymers (SBC) and styrene-isoprene block copolymers (SIS); and
(c) 0 to 5.0 wt.-% of at least one additive C;
wherein the wt.-% refers to the complete polymer blend,
and wherein the mold shrinkage of the polymer blend is reduced by at least 5% compared to the
mold shrinkage of the pure styrene copolymer A.
11. The article according to claim 10 , wherein the blend comprises:
(a) 91.5 to 99.4 wt.-% of at least one styrene copolymer A,
(b) 0.5 to 4.5 wt.-% of at least one copolymer B, and
(c) 0.1 to 5.0 wt.-% of at least one additive C.
12. The article according to claim 10 , wherein the article is an automotive part or a household part.
13. A polymer blend according to claim 1 , wherein
the Vicat softening temperature (VST B50) or the polymer blend is reduced by not more than 5 K compared to the VST B50 of the pure styrene copolymer A,
the melt volume flow rate MVR (220/10) of the polymer blend shows a delta of less than 15 ml/10 min compared to the MVR (220/10) of the pure styrene copolymer A, and
the E-modulus of the polymer blend shows a delta of less than 12% compared to the E-modulus of the pure styrene copolymer A.
14. A polymer article according to claim 10 , wherein
the Vicat softening temperature (VST B50) or the polymer blend is reduced by not more than 5 K compared to the VST B50 of the pure styrene copolymer A,
the melt volume flow rate MVR (220/10) of the polymer blend shows a delta of less than 15 ml/10 min compared to the MVR (220/10) of the pure styrene copolymer A, and
the E-modulus of the polymer blend shows a delta of less than 12% compared to the E-modulus of the pure styrene copolymer A.