Solid electrolyte material and solid-state battery made therewith

1. A solid electrolyte material comprising a formula:

Li 1-a-b-c-d P a T b A c X d

wherein 0≤a≤0.129, 0≤b≤0.096, 0.316≤c≤0.484, and 0.012≤d≤0.125, and

wherein T is at least one element selected from the group consisting of P, As, Si, Ge, Al, and B; X is one or more halogens or N; A is one or more of S and Se; and the solid electrolyte material has peaks at 17.8°±0.75° and 19.2°±0.75° in X-ray diffraction measurement with Cu-Kα(1,2)=1.5418 Å.

2. The solid electrolyte material of claim 1 , wherein a=0.111, b=0, c=0.444, d=0.056, A=S, and X=Cl.

3. The solid electrolyte material of claim 1 , further comprising at least one of glass ceramic phases, crystalline phases and mixed phases.

4. The solid electrolyte material of claim 1 , wherein mixed phases comprise crystalline phases containing peaks at 20.2°±0.75° and 23.6°±0.75°, and/or 21.0°±0.75° and 28.0°±0.75°, and/or 17.5°±0.75° and 18.2°±0.75° in X-ray diffraction measurement with Cu-Kα(1,2)=1.5418 Å.

5. The solid electrolyte material of claim 4 , wherein a ratio of peak intensity at 19.2°±0.75° to a peak at 17.5°±0.75° is 1 or more.

6. A lithium solid-state battery comprising a positive electrode active material layer containing a positive electrode active material; a negative electrode active material layer containing a negative electrode active material; and a solid electrolyte layer disposed between the positive electrode active material layer and the negative electrode active material layer, wherein at least one of the positive electrode active material layer, the negative electrode active material layer, and the solid electrolyte layer comprises the solid electrolyte material according to claim 1 .

7. The lithium solid-state battery of claim 6 , wherein the solid electrolyte layer comprises about 10% to 100% by volume of the solid electrolyte material.

8. The lithium solid-state battery of claim 6 , wherein the solid electrolyte material further comprises a binder.

9. The lithium solid-state battery of claim 8 , wherein the binder is selected from a group consisting of polyvinyl chloride, polyaniline, poly(methyl methacrylate), nitrile butadiene rubber, styrene-butadiene rubber, polyvinylidene fluoride, polystyrene, poly(ethylene) oxide, and self-healing polymers.

10. The lithium solid-state battery of claim 6 , wherein a thickness of the solid electrolyte layer is between about 1 μm to 1000 μm.

11. A method for producing a sulfide solid electrolyte material including glass ceramics, the sulfide solid electrolyte material comprising a formula:

Li 1-a-b-c-d P a T b A c X d , wherein 0≤a≤0.129, 0≤b≤0.096, 0.316≤c≤0.484, and 0.012≤d≤0.125,

wherein T is at least one of P, As, Si, Ge, Al, and B; X is one or more halogens or N; A is one or more of S and Se; the method comprising

mixing and milling a raw material composition containing an element A or compound Li 2 A, an element T or sulfide of T, and a compound LiX or Li 3 N to render the mixture amorphous under x-ray diffraction; and

heating the sulfide glass at a heat treatment temperature equal to or greater than a crystallization temperature of the sulfide glass to synthesize the glass ceramics having peaks at 17.8°±0.75° and 19.2°±0.75° in X-ray diffraction measurement with Cu-Kα(1,2)=1.5418 Å.

12. The method of claim 11 , wherein the raw material composition is mixed and milled for a predetermined period of time.

13. The method of claim 12 , wherein the predetermined period of time is between about 10 minutes to 60 hours.

14. The method of claim 11 , wherein the raw material composition is mixed and milled at a predetermined temperature.

15. The method of claim 14 , wherein the predetermined temperature is between about 20 to 120 degrees Celsius.

16. The method of claim 11 , wherein heating the sulfide glass is performed at a period of time between about one minute to 24 hours.

17. The method of claim 11 , wherein heating the sulfide glass is conducted in an inert gas atmosphere.

18. The method of claim 17 , wherein the inert gas atmosphere is an argon or nitrogen atmosphere.

19. The method of claim 11 , wherein heating the sulfide glass is conducted under vacuum.

20. The method of claim 11 , wherein the raw material composition is mixed and milled in a planetary ball-milling machine or an attritor mill.