Cold-rolled steel sheet with excellent formability, galvanized steel sheet, and manufacturing method thereof

1. A cold-rolled steel sheet, comprising, by weight percent (wt %), 0.06 to 0.15% of carbon (C), more than 0% and 1.2% or less of silicon (Si), 1.7 to 2.7% of manganese (Mn), more than 0% and 0.15% or less of molybdenum (Mo), more than 0% and 1.0% or less of chromium (Cr), 0.1% or less of phosphorus (P), 0.01% or less of sulfur (S), 0.001 to 0.04% of titanium (Ti), 0.001 to 0.04% of niobium (Nb), 0.01% or less of nitrogen (N), more than 0% and 0.01% or less of boron (B), and a remainder of Fe and unavoidable impurities,

wherein contents of the Si, the C, the Mn, the Mo and the Cr at a position of (¼) thickness of the cold-rolled steel sheet satisfy the following Relationship 1:

([Si]+[C]×3)/([Mn]+[Mo]+[Cr])>0.18

wherein [Si], [C], [Mn], [Mo] and [Cr] indicate contents, in weight percent, of Si, C, Mn, Mo, and Cr, respectively,

wherein the cold-rolled steel sheet includes: a microstructure consisting of, in area percent, 10 to 70% of a ferrite phase, 10 to 50% of a bainite phase and a retained austenite phase, and a remainder of a fresh martensite phase, and

a ratio (Mb/Mt) of a fresh martensite phase (Mb) adjacent to the bainite phase to a total fresh martensite phase (Mt) is 60% or more.

2. A cold-rolled steel sheet, comprising, by weight percent (wt %), 0.06 to 0.15% of carbon (C), more than 0% and 1.2% or less of silicon (Si), 1.7 to 2.7% of manganese (Mn), more than 0% and 0.15% or less of molybdenum (Mo), more than 0% and 1.0% or less of chromium (Cr), 0.1% or less of phosphorus (P), 0.01% or less of sulfur (S), 0.001 to 0.04% of titanium (Ti), 0.001 to 0.04% of niobium (Nb), 0.01% or less of nitrogen (N), more than 0% and 0.01% or less of boron (B), and a remainder of Fe and unavoidable impurities,

wherein contents of the Si, the C, the Mn, the Mo and the Cr at a position of (¼) thickness of the cold-rolled steel sheet satisfy the following Relationship 1:

([Si]+[C]×3)/([Mn]+[Mo]+[Cr])>0.18  Relationship 1:

where [Si], [C], [Mn], [Mo] and [Cr] indicate contents, in weight percent, of Si, C, Mn, Mo, and Cr, respectively,

wherein the cold-rolled steel sheet includes: a microstructure consisting of, in area percent, 10 to 70% of a ferrite phase, 10 to 50% of a bainite phase and a retained austenite phase, and a remainder of a fresh martensite phase, and

a ratio (Ms/Mt) of a fresh martensite phase (Ms) having an average particle size of 3 μm or less to a total fresh martensite phase (Mt) is 60% or more.

3. A cold-rolled steel sheet, comprising, by weight percent (wt %), 0.06 to 0.15% of carbon (C), more than 0% and 1.2% or less of silicon (Si), 1.7 to 2.7% of manganese (Mn), more than 0% and 0.15% or less of molybdenum (Mo), more than 0% and 1.0% or less of chromium (Cr), 0.1% or less of phosphorus (P), 0.01% or less of sulfur (S), 0.001 to 0.04% of titanium (Ti), 0.001 to 0.04% of niobium (Nb), 0.01% or less of nitrogen (N), more than 0% and 0.01% or less of boron (B), more than 0% and 1.0% or less of aluminum (sol. Al), more than 0% and 0.05% or less of antimony (Sb), and a remainder of Fe and unavoidable impurities,

wherein contents of the Si, the C, the Mn, the Mo and the Cr at a position of (¼) thickness of the cold-rolled steel sheet satisfy the following Relationship 1:

([Si]+[C]×3)/([Mn]+[Mo]+[Cr])>0.18

where [Si], [C], [Mn], [Mo] and [Cr] indicate contents of Si, C, Mn, Mo, and Cr, respectively,

wherein the cold-rolled steel sheet includes: a microstructure consisting of, in area percent, 10 to 70% of a ferrite phase, 10 to 50% of a bainite phase and a retained austenite phase, and a remainder of a fresh martensite phase, and a ratio (Mb/Mt) of a fresh martensite phase (Mb) adjacent to the bainite phase to a total fresh martensite phase (Mt) is 60% or more, and

wherein a strain hardening coefficient (n), elongation (El), tensile strength (TS), and a yield ratio (YR), each measured at a strain of 4 to 6%, satisfy the following Relationship 2:

n×El×TS/YR≥ 2500.

4. The cold-rolled steel sheet according to claim 1 , further comprising, by wt %, more than 0% and 1.0% or less of aluminum (sol. Al), and more than 0% and 0.05% or less of antimony (Sb).

5. The cold-rolled steel sheet according to claim 1 , wherein a ratio (Ms/Mt) of a fresh martensite phase (Ms) having an average particle size of 3 μm or less to the total fresh martensite phase (Mt) is 60% or more.

6. The cold-rolled steel sheet according to claim 1 , wherein a strain hardening coefficient (n), elongation (El), tensile strength (TS), and a yield ratio (YR), each measured at a strain of 4 to 6%, satisfy the following Relationship 2:

n×El×TS/YR≥ 2500.

7. A galvanized steel sheet comprising: the cold-rolled steel sheet of claim 1 ; and a galvanized layer formed on a surface of the cold-rolled steel sheet.

8. The cold-rolled steel sheet according to claim 2 , further comprising, by wt %, more than 0% and 1.0% or less of aluminum (sol. Al), and more than 0% and 0.05% or less of antimony (Sb).

9. The cold-rolled steel sheet according to claim 2 , wherein a strain hardening coefficient (n), elongation (El), tensile strength (TS), and a yield ratio (YR), each measured at a strain of 4 to 6%, satisfy the following Relationship 2:

n×El×TS/YR≥ 2500.

10. A galvanized steel sheet comprising: the cold-rolled steel sheet of claim 4 ; and a galvanized layer formed on a surface of the cold-rolled steel sheet.

11. The cold-rolled steel sheet according to claim 3 , wherein the fresh martensite phase (Mb) has an average particle size of 3 μm or less.

12. The galvanized steel sheet according to claim 7 , wherein the galvanized layer includes: an alloyed galvanized layer.

13. The galvanized steel sheet according to claim 10 , wherein the galvanized layer includes: an alloyed galvanized layer.