Ultra-Low Petroleum Plastics
Plastic-like compositions having ultra-low contents of petroleum derived materials are provided. The materials comprise up to about 80% by weight of an inorganic salt having an average particle size between about 0.001 and about 300 μm and a plastic binder. The compositions have a low propensity to ignite or smoke in the presence of heat or flame.
1 .- 69 . (canceled)
70 . A method of passing a flame test, the method comprising:
providing a non-intumescent composition comprising:
(a) about 10 to about 80% by weight of one or more polyurethane polymers;
(b) about 30 to about 60% by weight of ammonium sulfate, the ammonium sulfate having an average particle size from about 0.1 to about 100 μm; and
(c) one or more additives selected from the group consisting of plasticizers, stabilizers, fillers, blending resins, pigments, and impact modifiers;
subjecting the composition to the flame test; and
passing the flame test,
wherein the test is one or more of (i) ASTM E-84 test; (ii) UL-94 test; and (iii) U.S. Government standard for flammability resistance FAR 25.853.
71 . The method according to claim 70 , wherein the composition passes the ASTM E-84 with a Class A rating.
72 . The method according to claim 70 , wherein:
(I) subjecting the composition to the ASTM E-84 test comprises subjecting the composition to ASTM E-84 flame spread and smoke evolution testing; and
(II) the composition passes the ASTM E-84 test by providing no evidence of progressive combustion after 30 minutes under the conditions of (I).
73 . The method according to claim 71 , wherein:
(I) subjecting the composition to the ASTM E-84 test comprises subjecting the composition to ASTM E-84 flame spread and smoke evolution testing; and
(II) the composition passes the ASTM E-84 test by providing no evidence of progressive combustion after 30 minutes under the conditions of (I).
74 . The method according to claim 70 , wherein:
(I) subjecting the composition to the U.S. Government standard for flammability resistance FAR 25.853 test comprises subjecting the composition to edge burning by a flame maintained at 1550° F. for a period of 60 seconds; and
(II) the composition passes the U.S. Government standard for flammability resistance FAR 25.853 test by being self-extinguishing before 15 seconds and non-dripping under the conditions set forth in (I).
75 . The method according to claim 70 , wherein:
(I) subjecting the composition to the U.S. Government standard for flammability resistance FAR 25.853 test comprises subjecting the composition to edge burning by a flame maintained at 1550° F. for a period of 60 seconds; and
(II) the composition passes the U.S. Government standard for flammability resistance FAR 25.853 test by undergoing no flaming or dripping under the conditions set forth in (I).
76 . The method according to claim 70 , wherein:
(I) subjecting the composition to the U.S. Government standard for flammability resistance FAR 25.853 test comprises subjecting the composition to edge burning by a flame maintained at 1550° F. for a period of 12 seconds; and
(II) the composition passes the U.S. Government standard for flammability resistance FAR 25.853 test by being self-extinguishing before 15 seconds and non-dripping under the conditions set forth in (I).
77 . The method according to claim 70 , wherein:
(I) subjecting the composition to the U.S. Government standard for flammability resistance FAR 25.853 test comprises subjecting the composition to edge burning by a flame maintained at 1550° F. for a period of 12 seconds; and
(II) the composition passes the U.S. Government standard for flammability resistance FAR 25.853 test by undergoes no flaming or dripping under the conditions set forth in (I).