Porous polyimide film and battery
A porous polyimide film has an acid value within a range of 7 mgKOH/g to 20 mgKOH/g determined by acid-base titration, contains a metal group including alkali metals excluding Li, an alkaline earth metals, and silicon at a total content of 100 ppm or less relative to the porous polyimide film, and has a moisture absorption ratio of 0.5% or less.
1. A porous polyimide film comprising:
the porous polyimide film having an acid value within a range of 7 mgKOH/g to 20 mgKOH/g determined by acid-base titration, containing a metal group including alkali metals excluding Li, alkaline earth metals, and silicon at a total content of 100 ppm or less relative to the porous polyimide film, and having a moisture absorption ratio of 0.5% or less.
2. The porous polyimide film according to claim 1 , wherein the acid value is within a range of 12 mgKOH/g to 20 mgKOH/g.
3. The porous polyimide film according to claim 1 , wherein the tensile strength of the porous polyimide film is within a range of 10 N/mm 2 to 100 N/mm 2 .
4. The porous polyimide film according to claim 1 , wherein an average thickness of the porous polyimide film is within a range of 10 μm to 1000 μm.
5. The porous polyimide film according to claim 1 , wherein an average thickness of the porous polyimide film is within a range of 20 μm to 500 μm.
6. The porous polyimide film according to claim 1 , wherein the air permeation speed of the porous polyimide film is 25 seconds or less.
7. The porous polyimide film according to claim 1 , wherein a porosity of the porous polyimide film is within a range of 50% to 80%.
8. The porous polyimide film according to claim 1 , wherein a molar ratio (structural unit derived from tetracarboxylic dianhydride/structural unit derived from diamine) of a structural unit derived from tetracarboxylic dianhydride to a structural unit derived from diamine, both constituting a polyimide resin of the porous polyimide film, is within a range of 1.00 to 1.15.
9. The porous polyimide film according to claim 8 , wherein the molar ratio is within a range 1.06 to 1.15.
10. A porous polyimide film,
wherein a molar ratio (structural unit derived from tetracarboxylic dianhydride/structural unit derived from diamine) of a structural unit derived from tetracarboxylic dianhydride to a structural unit derived from diamine, both constituting a polyimide resin of the porous polyimide film, is within a range of 1.00 to 1.15, a total content of a metal group including alkali metals excluding Li, alkaline earth metals, and silicon is 100 ppm or less relative to the porous polyimide film, and a moisture absorption ratio of the porous polyimide film is 0.5% or less.
11. The porous polyimide film according to claim 10 , wherein the molar ratio is within a range 1.06 to 1.15.
12. A battery comprising the porous polyimide film according to claim 1 .
13. The battery according to claim 12 , wherein the battery is selected from a lithium ion secondary battery and an all-solid-state battery.
14. The battery according to claim 13 , wherein the porous polyimide film is a separator, and the battery is a lithium ion secondary battery.