Processes for preparing lithium hydroxide

1. A process for preparing lithium hydroxide, said process comprising:

submitting an aqueous composition comprising lithium sulphate to an electrolysis under conditions suitable for converting at least a portion of said lithium sulphate into lithium hydroxide;

wherein during said electrolysis, said aqueous composition comprising lithium sulphate is at least substantially maintained at a pH having a value of about 1 to about 4;

wherein said aqueous composition comprising lithium sulphate is prepared by a process comprising:

leaching an acid roasted lithium-containing material with water so as to obtain an aqueous composition comprising Li + and at least one metal ion, wherein said lithium-containing material is a material that has been previously reacted with H 2 SO 4 ;

reacting said aqueous composition comprising Li + and said at least one metal ion with a base so as to obtain a pH of about 4.5 to about 6.5 and thereby at least partially precipitating said at least one metal ion under the form of at least one hydroxide so as to obtain a precipitate comprising said at least one hydroxide and an aqueous composition comprising Li + and having a reduced content of said at least one metal ion, and separating said aqueous composition from said precipitate comprising said at least one hydroxide;

reacting said aqueous composition comprising Li + and having said reduced content of said at least one metal ion with another base so as to obtain a pH of about 9.5 to about 11.5, thereby at least partially precipitating at least one metal ion so as to obtain a precipitate and an aqueous composition comprising Li + and having a reduced content of said at least one metal ion;

seperating said aqueous composition from said precipitate; and

contacting said aqueous composition comprising Li + and having said reduced content of said at least one metal ion with an ion-exchange resin so as to at least partially remove at least one metal ion from said composition, thereby obtaining said aqueous composition comprising lithium sulphate.

2. The process of claim 1 , further comprising:

reacting said aqueous composition comprising Li + and having said reduced content of said at least one metal ion with said another base and with at least one metal carbonate, thereby at least partially precipitating at least one metal ion under the form of at least one carbonate so as to obtain a precipitate comprising said at least one carbonate and an aqueous composition comprising Li + and having a reduced content of said at least one metal ion; and

separating said aqueous composition from said precipitate comprising said at least one carbonate.

3. The process of claim 1 , wherein during said electrolysis, said pH is at least substantially maintained at a value of about 2 to about 4.

4. The process of claim 1 , wherein during said process said aqueous composition comprising lithium hydroxide is at least substantially maintained at a concentration of lithium hydroxide of about 35 to about 70 g/L.

5. The process of claim 1 , wherein during said process said aqueous composition comprising sulphuric acid is at least substantially maintained at a concentration of sulphuric acid of about 20 to about 50 g/L.

6. The process of claim 1 , wherein during said process said aqueous composition comprising lithium sulphate is at least substantially maintained at a concentration of lithium sulphate of about 10 to about 20 g/L.

7. The process of claim 1 , wherein during said process, temperature of said aqueous composition comprising lithium sulphate is at least substantially maintained at a value of about 20 to about 80° C.

8. The process of claim 1 , wherein during said process, temperature of said aqueous composition comprising lithium sulphate is at least substantially maintained at a value of about 50 to about 60° C.

9. The process of claim 1 , wherein during said process electrical current is at least substantially maintained at a density of about 400 to about 3000 A/m 2 .

10. The process of claim 1 , wherein during said process electrical current is at least substantially maintained at a constant value.

11. The process of claim 1 , wherein during said process voltage is at least substantially maintained at a constant value.

12. The process of claim 1 , wherein an anolyte used during said process comprises ammonia.

13. The process of claim 1 , further comprising adding ammonia in an anolyte used for said process, thereby generating an ammonium salt.

14. The process of claim 13 , wherein said ammonium salt is (NH 4 ) 2 SO 4 .

15. A process for preparing lithium hydroxide, said process comprising:

submitting an aqueous composition comprising a lithium compound to an electrolysis under conditions suitable for converting at least a portion of said lithium compound into lithium hydroxide;

wherein during said electrolysis, said aqueous composition comprising said lithium compound is at least substantially maintained at a pH having a value of about 1 to about 4;

wherein said aqueous composition comprising said lithium compound is prepared by a process comprising:

leaching an acid roasted lithium-containing material with water so as to obtain an aqueous composition comprising Li + and at least one metal ion;

reacting said aqueous composition comprising Li + and said at least one metal ion with a base so as to obtain a pH of about 4.5 to about 6.5 and thereby at least partially precipitating said at least one metal ion under the form of at least one hydroxide so as to obtain a precipitate comprising said at least one hydroxide and an aqueous composition comprising Li + and having a reduced content of said at least one metal ion, and separating said aqueous composition from said precipitate comprising said at least one hydroxide;

reacting said aqueous composition comprising Li + and having said reduced content of said at least one metal ion with another base so as to obtain a pH of about 9.5 to about 11.5, thereby at least partially precipitating at least one metal ion so as to obtain a precipitate and an aqueous composition comprising Li + and having a reduced content of said at least one metal ion;

separating said aqueous composition from said precipitate; and

contacting said aqueous composition comprising Li + and having said reduced content of said at least one metal ion with an ion exchange resin so as to at least partially remove at least one metal ion from said composition, thereby obtaining said aqueous composition comprising said lithium compound.

16. The process of claim 15 , further comprising:

reacting said aqueous composition comprising Li + and having said reduced content of said at least one metal ion with said another base and with at least one metal carbonate, thereby at least partially precipitating at least one metal ion under the form of at least one carbonate so as to obtain a precipitate comprising said at least one carbonate and an aqueous composition comprising Li + and having a reduced content of said at least one metal ion; and

separating said aqueous composition from said precipitate comprising said at least one carbonate.

17. The process of claim 15 , wherein during said electrolysis, said pH is at least substantially maintained at a value of about 2 to about 4.

18. The process of claim 15 , wherein said aqueous composition comprising said lithium compound comprises lithium sulphate, lithium chloride, lithium fluoride, lithium carbonate, lithium bicarbonate, lithium acetate, lithium stearate or lithium citrate.