Antimicrobial glaze and porcelain enamel via double layer glaze with high zinc content
A cost-effective and practical antimicrobial glaze system and glazing process is disclosed herein. The antimicrobial glaze/enamel may comprise at least two layers: a base layer and a top layer. The base layer may contain a typical or normal glaze widely used in sanitary ware, having a low level of zinc oxide. The base layer glaze may be directly sprayed on the clay body surface. A thin top glaze layer is sprayed on top of the base glaze layer and the top layer may contain a high level of zinc oxide.
1. Sanitary ware comprising a multilayer antimicrobial ceramic glaze, the ceramic glaze comprising
a base glaze layer containing from 0.0 percent by weight to about 8.0 percent by weight ZnO; and
a top glaze layer containing from about 8.0 percent by weight to about 35.0 weight percent ZnO,
wherein a total ZnO content in the multilayer glaze is less than 5.0 weight percent.
2. The sanitary ware of claim 1 , wherein the top layer contains from about 10.0 weight percent to about 25.0 weight percent ZnO.
3. The sanitary ware of claim 1 , wherein the base layer contains ZnO.
4. The sanitary ware of claim 1 , wherein the base layer contains from about 0.0 weight percent to about 6.0 weight percent ZnO.
5. The sanitary ware of claim 1 , wherein the ceramic glaze is substantially free of surface defects.
6. The sanitary ware of claim 1 , wherein the base glaze layer is from about 300 μm to about 1000 μm thick.
7. The sanitary ware of claim 1 , wherein the base glaze layer is from about 300 μm to about 600 μm thick.
8. The sanitary ware of claim 1 , wherein the top glaze layer is from about 25 μm to about 250 μm thick.
9. The sanitary ware of claim 1 , wherein the top glaze layer is from about 25 μm to about 150 μm thick.
10. The sanitary ware of claim 1 , wherein the top glaze layer is from about 100 μm to about 200 μm thick.
11. The sanitary ware of claim 1 , wherein the top glaze layer is from about 150 μm to about 300 μm thick.
12. The sanitary ware of claim 1 , wherein the top glaze layer is from about 200 μm to about 300 μm thick.
13. The sanitary ware of claim 1 , wherein a top 10 μm of the top glaze layer contains more than 8 weight percent and less than 35.0 weight percent ZnO.
14. The sanitary ware of claim 1 , wherein a top 10 μm of the top glaze layer contains more than 8 weight percent and less than 15.0 weight percent ZnO.
15. The sanitary ware of claim 1 , wherein the top glaze layer includes a source of ions selected from one or more of Hg, Ag, Cu, Fe, Pb, Bi, and rare earths.
16. Sanitary ware comprising a multilayer antimicrobial ceramic glaze, the ceramic glaze comprising
a base glaze layer containing from 0.0 percent by weight to about 8.0 percent by weight ZnO; and
a top glaze layer containing from about 8.0 percent by weight to about 35.0 weight percent ZnO,
wherein a top 10 μm of the top glaze layer contains more than 8 weight percent and less than 35.0 weight percent ZnO.
17. The sanitary ware of claim 16 , wherein a top 10 μm of the top glaze layer contains more than 8 weight percent and less than 15.0 weight percent ZnO.
18. The sanitary ware of claim 16 , wherein the top layer contains from about 10.0 weight percent to about 25.0 weight percent ZnO.
19. The sanitary ware of claim 16 , wherein the base glaze layer is from about 300 μm to about 1000 μm thick.
20. The sanitary ware of claim 16 , wherein the top glaze layer is from about 25 μm to about 300 μm thick.
21. The sanitary ware of claim 16 , wherein a total ZnO content in the multilayer glaze is less than 5.0 weight percent.