Preparation method for heat pipe
Methods for preparing a heat pipe are provided. The methods may include forming a metal foam on a surface of a first metal sheet using a slurry, placing the first metal sheet on a second metal sheet, and bonding outer portions of the first and second metal sheets. The surface of the first metal sheet faces the second metal sheet.
1. A method for preparing a heat pipe, the method comprising:
forming a metal foam directly on a surface of a first metal sheet using a slurry, wherein the slurry comprises metal powder, a binder, and a dispersant;
placing the first metal sheet on a second metal sheet, wherein the surface of the first metal sheet faces the second metal sheet; and
bonding outer portions of the first and second metal sheets,
wherein forming the metal foam directly on the surface of the first metal sheet comprises forming a metal foam precursor on the surface of the first metal sheet by applying the slurry directly onto the surface of the first metal sheet, and
wherein the slurry is devoid of a blowing agent.
2. The method of claim 1 , wherein forming the metal foam directly on the surface of the first metal sheet further comprises sintering the metal foam precursor.
3. The method of claim 2 , wherein the metal foam precursor is formed in the form of a film or sheet.
4. The method of claim 2 , wherein the sintering is performed at a temperature in a range of 500° C. to 2000° C.
5. The method of claim 2 , wherein forming the metal foam precursor comprises coating the slurry on the surface of the first metal sheet, and
wherein the method further comprises performing a drying process after forming the metal foam precursor and before sintering the metal foam precursor.
6. The method of claim 5 , wherein the drying process is performed at a temperature in a range of 50° C. to 250° C.
7. The method of claim 1 , wherein the slurry comprises 1 to 500 parts by weight of the binder relative to 100 parts by weight of the metal powder, and 10 to 2,000 parts by weight of the dispersant relative to 100 parts by weight of the binder.
8. The method of claim 1 , wherein the metal powder has an average particle diameter in a range of 0.1 μm to 200 μm.
9. The method of claim 1 , wherein the binder is alkyl cellulose, polyalkylene carbonate or a polyvinyl alcohol-based binder.
10. The method of claim 1 , wherein the dispersant is an alcohol.
11. The method of claim 1 , wherein the slurry further comprises a solvent.
12. The method of claim 1 , wherein the metal foam comprises a first metal foam, and
wherein the method further comprises forming a second metal foam directly on a surface of the second metal sheet, wherein the surface of the second metal sheet faces the first metal sheet.
13. The method of claim 1 wherein the metal foam has a porosity in a range of 60% to 99%.
14. The method of claim 1 , wherein the metal foam has a pore size in a range of 100 nm to 100 μm.
15. The method of claim 1 , wherein the metal foam has a thickness of 500 μm or less.
16. The method of claim 1 , wherein the heat pipe has a thickness in a range of 0.06 mm to 0.8 mm.
17. The method of claim 1 , wherein the metal powder comprises conductive magnetic metal powder.
18. The method of claim 1 , wherein the metal powder comprises at least one of powder of nickel, iron and cobalt.
19. The method of claim 1 , wherein the first metal sheet further comprises an inner portion between the outer portions, and
the metal foam is formed on the inner portion of the first metal sheet and is not formed on the outer portions of the first metal sheet.