Polyolefin microporous membrane with improved puncture elongation and thermomechanical properties and method for manufacturing the same
A polyolefin microporous membrane has a puncture elongation of not more than 2.30 mm. The temperature of the stress inflection point is not less than 80.0° C., and the stress peak value is not more than 1.8 gin thermomechanical analysis (TMA) measurement of the transverse direction of the polyolefin microporous membrane.
1. A polyolefin microporous membrane having a puncture elongation of not more than 2.30 mm, a temperature at a stress inflection point of not less than 80.0° C., and a stress peak value of not more than 1.8 g in thermomechanical analysis (TMA) measurement of a transverse direction of the polyolefin microporous membrane, wherein the polyolefin microporous membrane is a single layer excluding an inorganic coating layer at a measurement of the puncture elongation and the TMA measurement performed in constant length mode.
2. The polyolefin microporous membrane according to claim 1 wherein the puncture elongation is not more than 2.10 mm, the temperature at the stress inflection point is not less than 90.0° C., and the stress peak value is not more than 1.4 g in the TMA measurement of the transverse direction of the polyolefin microporous membrane.
3. The polyolefin microporous membrane according to claim 1 wherein the puncture elongation is not less than 0.5 mm, the temperature at the stress inflection point is not more than 180.0° C., and the stress peak value is not less than 0.3 g in the TMA measurement of the transverse direction of the polyolefin microporous membrane.
4. The polyolefin microporous membrane according to claim 1 wherein puncture strength per unit thickness is less than 70 gf/μm.
5. The polyolefin microporous membrane according to claim 4 wherein the puncture strength per unit thickness is not less than 10 gf/μm.
6. The polyolefin microporous membrane according to claim 1 wherein a stress peak value is not more than 2.0 g in TMA measurement of a machine direction of the polyolefin microporous membrane.
7. The polyolefin microporous membrane according to claim 6 wherein the stress peak value is not less than 0.3 g in TMA measurement of the machine direction of the polyolefin microporous membrane.
8. The polyolefin microporous membrane according to claim 6 , wherein puncture strength per unit thickness is less than 70 gf/μm.
9. The polyolefin microporous membrane according to claim 8 , wherein the puncture elongation is not less than 0.5 mm, the temperature at the stress inflection point is not more than 180.0° C., and the stress peak value is not less than 0.3 g in the TMA measurement of the transverse direction.
10. The polyolefin microporous membrane according to claim 9 , wherein the stress peak value is not less than 0.3 g in TMA measurement of the machine direction.
11. The polyolefin microporous membrane according to claim 10 , wherein the puncture strength per unit thickness is not less than 10 gf/μm.
12. A method for manufacturing a polyolefin microporous membrane according to claim 1 comprising the following steps:
(A) extruding a polyolefin composition comprising a polyolefin resin and a pore-forming material to form a gel-like sheet;
(B) biaxially stretching the gel-like sheet to form a stretched sheet;
(C) extracting the pore-forming material from the stretched sheet to form a porous membrane; and
(D) heat setting the porous membrane; wherein
strain rate in a machine direction in step (B) is not less than 20%/second and not more than 50%/second, and a ratio of the strain rate in the transverse direction in step (B) to the strain rate in the transverse direction in step (D) is not less than 2.0 and not more than 10.0.
13. The method of manufacturing a polyolefin microporous membrane according to claim 12 , wherein the polyolefin microporous membrane has a puncture elongation of not less than 0.5 mm, the temperature at the stress inflection point of not more than 180.0° C., a stress peak value of not less than 0.3 g in thermomechanical analysis (TMA) measurement of the transverse direction.
14. The method for manufacturing a polyolefin microporous membrane according to claim 12 wherein in step (B), the gel-like sheet is simultaneously biaxially stretched.
15. The method of manufacturing a polyolefin microporous membrane according to claim 14 , wherein the polyolefin microporous membrane has a puncture elongation of not less than 0.5 mm, the temperature at the stress inflection point of not more than 180.0° C., a stress peak value of not less than 0.3 g in thermomechanical analysis (TMA) measurement of the transverse direction.