Process for preparing a polypropylene composition
The invention relates to a process for producing a polypropylene composition by sequential polymerization the polypropylene composition having an improved balanced combination of high flowability, high stiffness and impact, and high level of optical properties.
1. A process for producing a polypropylene composition by sequential polymerization comprising the steps:
a) polymerizing in a first reactor monomers comprising propylene and optionally one or more comonomers selected from ethylene and C 4 -C 10 alpha-olefins, to obtain a first propylene polymer fraction having a comonomer content in the range of 0.0 to 1.8 wt %, and a MFR 2 in the range of from 15.0 to 40.0 g/10 min, as measured according to ISO 1133 at 230° C. under a load of 2.16 kg;
b) polymerizing in a second reactor monomers comprising propylene and one or more comonomers selected from ethylene and C 4 -C 10 alpha-olefins, in the presence of the first propylene polymer fraction, to obtain a second propylene polymer fraction having a comonomer content in the range of 2.0 to 12.0 wt %, wherein the ratio of the one or more comonomers to propylene (process comonomer ratio) in the second reactor is in the rage of 15.0 to 85.0 mol/kmol;
c) extruding the second propylene polymer fraction in the presence of at least one alpha-nucleating agent;
wherein the polypropylene composition has an MFR 2 in the range of from 15.0 to 60.0 g/10 min, as measured according to ISO 1133 at 230° C. under a load of 2.16 kg;
wherein the process is operated in the presence of a Ziegler-Natta catalyst with a transition metal of group 4 to 6 of the periodic table and the catalyst comprising an internal donor, wherein the internal donor is a non-phthalic internal donor; and
wherein the non-phthalic internal donor is selected from (di)esters of non-phthalic carboxylic (di)acids, wherein the (di)ester belongs to the group consisting of malonates, maleates, citraconates, glutarates, cyclohexene-1,2-dicarboxylates, derivatives thereof, and mixtures thereof.
2. The process according to claim 1 , wherein the comonomers in step a) and/or b) are selected from one or more comonomers comprising ethylene.
3. The process according to claim 1 , wherein:
a) the hydrogen/propylene (H 2 /C 3 ) ratio in the first reactor is in the range of 1.5 to 6.0 mol/kmol; and
b) the hydrogen/propylene (H 2 /C 3 ) ratio in the second reactor is in the range of 12.0 to 70.0 mol/kmol.
4. The process according to claim 1 , wherein the second propylene polymer fraction is extruded in the presence of an amount of the at least one alpha-nucleating agent in the range of from 0.01 to 1.0 wt %, relative to the total amount of polypropylene composition.
5. The process according to claim 1 , wherein the ratio of the one or more comonomers to propylene (process comonomer ratio) in the first reactor is 0.0 to 14.0 mol/kmol.
6. The process according to claim 1 , wherein the first reactor comprises a slurry reactor.
7. The process according to claim 1 , wherein the second reactor comprises a gas phase reactor.
8. The process according to claim 1 , wherein the catalyst further comprises a co-catalyst, an external donor, or a combination thereof.
9. The process according to claim 1 , wherein the comonomers in step a) and/or b) comprise solely ethylene.