Scratch-resistant styrene copolymer composition containing amide wax

1. A thermoplastic polymer composition (P) comprising:

(A) 90 to 99.9 wt.-% of at least one styrene-based copolymer;

(B) 0.1 to 10 wt.-% of an aliphatic wax additive comprising at least one aliphatic amide wax composition (B-1) having a melting point in the range of 80° C. to 115° C. and at least one aliphatic fatty acid ester composition (B-2) having a melting point in the range of 35° C. to 60° C.;

(C) 0 to 9.9 wt.-% of at least one colorant, dye, or pigment; and

(D) 0 to 3 wt.-% of at least one further additive,

wherein:

the constituents (A) to (D) sum up to 100 wt.-% of the thermoplastic polymer composition (P);

the weight ratio (B-1) to (B-2) is ≥0.9:1 to ≤2.2:1; and

the at least one styrene-based copolymer (A) is selected from poly(styrene-co-acrylonitrile) (SAN), poly(α-methyl styrene-co-acrylonitrile) (AMSAN), poly(styrene-co-methyl methacrylate) (SMMA), and mixtures thereof.

2. The thermoplastic polymer composition (P) according to claim 1 comprising:

(A) 93 to 99.9 wt.-% of at least one styrene-based copolymer;

(B) 0.1 to 7 wt.-% of an aliphatic wax additive comprising at least one aliphatic amide wax composition (B-1) having a melting point in the range of 80° C. to 115° C. and at least one aliphatic fatty acid ester composition (B-2) having a melting point in the range of 35° C. to 60° C.;

(C) 0 to 6.9 wt.-% of at least one colorant, dye, or pigment; and

(D) 0 to 3 wt.-% of at least one further additive,

wherein the constituents (A) to (D) sum up to 100 wt.-% of the thermoplastic polymer composition (P).

3. The thermoplastic polymer composition (P) according to claim 1 comprising:

(A) 95 to 99.8 wt.-% of at least one styrene-based copolymer;

(B) 0.2 to 5 wt.-% of an aliphatic wax additive comprising at least one aliphatic amide wax composition (B-1) having a melting point in the range of 80° C. to 115° C. and at least one aliphatic fatty acid ester composition (B-2) having a melting point in the range of 35° C. to 60° C.;

(C) 0 to 4.8 wt.-% of at least one colorant, dye, or pigment; and

(D) 0 to 3 wt.-% of at least one further additive;

wherein the constituents (A) to (D) sum up to 100 wt.-% of the thermoplastic polymer composition (P).

4. The thermoplastic polymer composition (P) of claim 1 comprising:

(A) 93 to 99.7 wt.-% of at least one styrene-based copolymer;

(B) 0.1 to 6.8 wt.-% of an aliphatic wax additive comprising at least one aliphatic amide wax composition (B-1) having a melting point in the range of 80° C. to 115° C. and at least one aliphatic fatty acid ester composition (B-2) having a melting point in the range of 35° C. to 60° C.;

(C) 0.1 to 5 wt.-% of at least one colorant, dye, or pigment; and

(D) 0.1 to 3 wt.-% of at least one further additive,

wherein the constituents (A) to (D) sum up to 100 wt.-% of the thermoplastic polymer composition (P).

5. The thermoplastic polymer composition (P) of claim 1 comprising:

(A) 95 to 98.8 wt.-% of at least one styrene-based copolymer;

(B) 0.2 to 2 wt.-% of an aliphatic wax additive comprising at least one aliphatic amide wax composition (B-1) having a melting point in the range of 80° C. to 115° C. and at least one aliphatic fatty acid ester composition (B-2) having a melting point in the range of 35° C. to 60° C.;

(C) 0.5 to 5 wt.-% of at least one colorant, dye, or pigment; and

(D) 0.5 to 3 wt.-% of at least one further additive,

wherein the constituents (A) to (D) sum up to 100 wt.-% of the thermoplastic polymer composition (P).

6. The thermoplastic polymer composition (P) according to claim 1 , wherein:

the at least one aliphatic amide wax composition (B-1) comprises amide compounds having the formula R 1 —CONH—R 2 , wherein R 1 and R 2 are each independently selected from aliphatic, saturated or unsaturated hydrocarbon groups having 1 to 30 carbon atoms; and

the at least one aliphatic fatty acid ester composition (B-2) comprises fatty acid ester compounds having the formula R 3 —CO—OR 4 , wherein R 3 and R 4 are each independently selected from aliphatic, saturated or unsaturated hydrocarbon groups having 1 to 45 carbon atoms.

7. The thermoplastic polymer composition (P) according to claim 6 , wherein:

the at least one aliphatic amide wax composition (B-1) comprises amide compounds having the formula R 1 —CONH—R 2 , wherein R 1 and R 2 are each independently selected from aliphatic, saturated or unsaturated hydrocarbon groups having 12 to 24 carbon atoms; and

the at least one aliphatic fatty acid ester composition (B-2) comprises fatty acid ester compounds having the formula R 3 —CO—OR 4 , wherein R 3 and R 4 are each independently selected from aliphatic, saturated or unsaturated hydrocarbon groups having 15 to 40 carbon atoms.

8. The thermoplastic polymer composition (P) according to claim 6 , wherein:

the at least one aliphatic amide wax composition (B-1) comprises amide compounds having the formula R 1 —CONH—R 2 , wherein R 1 and R 2 are each independently selected from aliphatic, saturated or unsaturated hydrocarbon groups having 16 to 20 carbon atoms; and

the at least one aliphatic fatty acid ester composition (B-2) comprises fatty acid ester compounds having the formula R 3 —CO—OR 4 , wherein R 3 and R 4 are each independently selected from aliphatic, saturated or unsaturated hydrocarbon groups having 25 to 35 carbon atoms.

9. The thermoplastic polymer composition (P) according to claim 1 , wherein an article prepared from the thermoplastic polymer composition (P) requires a minimum normal load of at least 300 g in a scratch resistance test following ISO 1518-1 realized with an Erichsen Linear Tester to achieve a full scratch mark on the surface of the article.

10. A process for the preparation of the thermoplastic polymer composition (P) according to claim 1 , wherein the process comprises at least the following steps:

a) providing the components (A) to (D) in the predetermined amounts to an optionally heatable mixing device; and

b) blending the components (A) to (D) in the optionally heatable mixing device at temperatures above the glass transition point of the components (A) to (D) to obtain the thermoplastic polymer composition (P).

11. A polymer composition, comprising 50 to 99 wt.-% of the thermoplastic polymer composition (P) according to claim 1 , and 50 to 1 wt.-% of at least one further thermoplastic polymer selected from polyolefins, polycarbonates, polyamides, and mixtures thereof.

12. A molded article, prepared from the thermoplastic polymer composition (P) according the polymer composition according to claim 11 .

13. The molded article according to claim 12 , wherein the molded article is prepared by an injection molding process.

14. A method of making components or articles for electronic devices, household goods, and automotive parts comprising the molded article according to claim 12 .

15. The method according to claim 14 , where the molded article is used in A/B/C pillars of automobiles.

16. A molded article, prepared from the thermoplastic polymer composition (P) according to claim 1 .

17. The molded article according to claim 16 , wherein the molded article is prepared by an injection molding process.

18. A method of making components or articles for electronic devices, household goods, and automotive parts comprising the molded article according to claim 16 .

19. The method according to claim 18 , where the molded article is used in A/B/C pillars of automobiles.

20. A method of making components or articles for electronic devices, household goods, and automotive parts comprising the thermoplastic polymer composition (P) according to claim 1 .