Impact modified styrene copolymer composition comprising polysiloxane additive having improved abrasion characteristics

1. A thermoplastic polymer composition (P) comprising:

(A) 82 to 99.75 wt.-% of at least one styrene-based polymer composition (A) comprising:

(A-1) 30 to 40 wt.-%, based on the total weight of the styrene-based polymer composition (A), of at least two styrene-based graft copolymers (A-1), wherein the graft copolymer (A-1) is poly(acrylonitrile-styrene-acrylic ester) (ASA), wherein the graft copolymer (A-1) comprises at least two graft copolymers (A-1-I) and (A-1-II), wherein:

(i) graft copolymer (A-1-I) comprises ASA rubber particles having a mean particle diameter D 50 from 50 to 180 nm, and

(ii) graft copolymer (A-1-II) comprises ASA rubber particles having a mean particle diameter D 50 from 200 to 800 nm, and

(A-2) 60 to 70 wt.-%, based on the total weight of the styrene-based polymer composition (A), of a thermoplastic polymer (A-2) comprising 40 to 60 wt.-% of polystyrene-acrylonitrile) (SAN) and 60 to 40 wt.-% poly(α-methyl styrene-acrylonitrile) (AMSAN), based on the total weight of the thermoplastic polymer (A-2);

(B) 0.25 to 18 wt.-% of at least one organopolysiloxane compound selected from a poly(dialkylsiloxane) compound with each alkyl group independently comprising 1 to 10 carbon atoms and having a weight average molecular weight Mw of 100,000 g/mol to 1,000,000 g/mol, determined by gel permeation chromatography (GPC) relative to polystyrene as standard and THF as solvent;

(C) 0 to 10 wt.-% of at least one colorant, dye, or pigment; and

(D) 0 to 3 wt.-% of at least one further additive;

wherein the constituents (A) to (D) sum up to 100 wt.-% of the thermoplastic polymer composition (P).

2. The thermoplastic polymer composition (P) according to claim 1 comprising:

(A) 89 to 98.5 wt.-% of a styrene-based polymer composition (A) comprising t least one graft copolymer (A-1);

(B) 0.5 to 10 wt.-% of at least one organopolysiloxane compound;

(C) 0.5 to 5 wt.-% of at least one colorant, dye or pigment; and

(D) 0.5 to 3 wt.-% of at least one further additive;

wherein the constituents (A) to (D) sum up to 100 wt.-% of the thermoplastic polymer composition (P).

3. The thermoplastic polymer composition (P) according to claim 1 , wherein the organopolysiloxane compound (B) is selected from poly(dimethylsiloxane), poly(diethylsiloxane), poly(dipropylsiloxane), poly(dibutylsiloxane), and mixtures thereof.

4. The thermoplastic polymer composition (P) according to claim 1 , wherein the surface of the thermoplastic polymer composition (P) has a residual gloss of more than 30% after abrasion was effected according to norm PV3975 compared to the surface of the non-abraded thermoplastic polymer composition (P).

5. The thermoplastic polymer composition (P) according to claim 1 , wherein the melt volume-flow rate (MVR, 220 ml/10 min according to ISO 1133) of the thermoplastic polymer composition (P) is increased by a factor of at least 1.5 compared to the melt volume-flow rate of a thermoplastic polymer composition which does not comprise the at least one organopolysiloxane compound (B).

6. The thermoplastic polymer composition (P) according to claim 1 , wherein the Vicat softening temperature (VST B50, according to DIN EN ISO 306) of the thermoplastic polymer composition (P) is reduced by less than 5′C compared to the Vicat softening temperature of a thermoplastic polymer composition which does not comprise the at least one organopolysiloxane compound (B).

7. The thermoplastic polymer composition (P) according to claim 1 , wherein the Charpy notched impact strength of the thermoplastic polymer composition (P) is reduced by less than 4 kl/m 2 , compared to the Charpy notched impact strength of a thermoplastic polymer composition which does not comprise the at least one organopolysiloxane compound (B).

8. A process for preparing a thermoplastic polymer composition (P) according to claim 1 , wherein the process comprises at least the following steps:

a) providing the components (A) to (D) in the predetermined amounts to an optionally heatable mixing device; and

b) blending the components (A) to (D) in the optionally heatable mixing device at temperatures above the glass transition point of the components (A) to (D) to obtain the thermoplastic polymer composition (P).

9. A molded article, prepared from a thermoplastic polymer composition (P) according to claim 1 .

10. A method of making components or articles for electronic devices, household goods, and automotive parts comprising the thermoplastic polymer composition (P) according to claim 1 .

11. A method of making components or articles for electronic devices, household goods, and automotive parts comprising the molded article according to claim 9 .

12. The molded article according to claim 9 , wherein the molded article is a component or article for electronic devices, household goods, and automotive parts.

13. The thermoplastic polymer composition (P) according to claim 1 , wherein the thermoplastic polymer composition (P) comprises as constituent (B) 0.25 to 12 wt.-% of the at least one organopolysiloxane compound.

14. The thermoplastic polymer composition (P) according to claim 1 , wherein the thermoplastic polymer composition (P) comprises as constituent (B) 0.25 to 5 wt.-% of the at least one organopolysiloxane compound.

15. The thermoplastic polymer composition (P) according to claim 1 , wherein the thermoplastic polymer composition (P) comprises as constituent (B) 0.25 to 6 wt.-% of the at least one organopolysiloxane compound.

16. The thermoplastic polymer composition (P) according to claim 1 , wherein the thermoplastic polymer composition (P) comprises as constituent (B) 0.25 to 3 wt.-% of the at least one organopolysiloxane compound.