Polypropylene copolymers with improved stiffness and impact behaviour
The present invention is directed towards random-heterophasic propylene copolymers with a specific ratio of stiffness to impact balance and specific relation between glass transition temperature and comonomer content. The invention is further directed to articles comprising said random-heterophasic propylene copolymer and their use.
1. Random-heterophasic propylene copolymer comprising:
a. 75.0-90.0 wt. % of a random propylene copolymer (A) as matrix, wherein the random propylene copolymer (A) comprises ethylene and/or C4 to C8 α-olefin as comonomers and is characterized by a comonomer content in the range of 3.2 to 4.0 wt. %, and
b. 10.0-25.0 wt. % of a elastomeric propylene copolymer (B) being dispersed in (A),
wherein the random-heterophasic propylene copolymer has at least two glass transition temperatures Tg(1) and Tg(2), wherein the first glass transition temperature Tg(1) relates to the matrix (A) while the second glass transition temperature Tg(2) relates to the dispersed elastomeric propylene copolymer (B), wherein further the second glass transition temperature fulfils the inequation (I),
(Tg2)/(° C.)>14.0−[2.1*(C(XCS))/(wt.-%)] (I)
wherein Tg(2) is the second glass transition temperature of the random-heterophasic propylene copolymer and C(XCS) is the comonomer content in [wt. %] of the xylene cold soluble fraction (XCS) of the random-heterophasic propylene copolymer,
wherein the second glass transition temperature and the Charpy notched impact strength fulfil the inequation (II)
(Tg2)/(° C.)+3*NIS/(kJ/m 2 )>0 (II)
wherein Tg(2) is the second glass transition temperature of the random-heterophasic propylene copolymer and NIS is the Charpy Notched Impact Strength determined according to ISO179/1eA at +23° C.;
wherein the random-heterophasic propylene copolymer has a xylene soluble content determined according to ISO 16152 (25° C.) in the range of 18.0-28.0 wt. %, wherein the fraction soluble in xylene (i) has an intrinsic viscosity (IV) in the range of 1.70-2.50 dl/g when measured according to ISO 1628; and
a Flexural Modulus in the range of 625 MPa to 1000 MPa when measured according to ISO 178.
2. Random-heterophasic propylene copolymer according to claim 1 , having a comonomer content in the range of 7.0-11.0 wt. %.
3. Random-heterophasic propylene copolymer according to claim 1 , wherein the fraction soluble in xylene (ii) has a comonomer content (C(XCS)) of 23.0-35.0 wt. %.
4. Random-heterophasic propylene copolymer according to claim 1 , having a crystallisation temperature (Tc) of at least 107° C.
5. Random-heterophasic propylene copolymer according to claim 1 , having a melting temperature of at least 135° C.
6. Random-heterophasic propylene copolymer according to claim 1 , having a Melt Flow Rate 230/2.16, determined according to ISO1133, of 0.5-15.0 g/10 min.
7. Random-heterophasic propylene copolymer according to claim 1 , wherein the random-heterophasic propylene copolymer has:
a. an Charpy notched impact Strength (NIS) of at least 14.0 kJ/m 2 when measured according to ISO179/1eA at +23° C. and/or
b. a Mechanical Performance Index in Injection Moulding (MPI IM ) of at least 1600.
8. Random-heterophasic propylene copolymer according to claim 1 , wherein the random-heterophasic propylene copolymer is characterized by having:
a. a Tensile Modulus of at least 320 MPa when measured according to ISO527 on 50 μm cast films in transverse direction (TD) and/or
b. a relative penetration energy W tot of at least 40.0 J/mm when measured according to Dyna test +23° C.) and/or
c. a Mechanical Performance Index on Films (MPI F ) of at least 3000.
9. Article comprising the random-heterophasic propylene copolymer according to claim 1 .