Positive electrode active material for nonaqueous electrolyte secondary battery, positive electrode for nonaqueous electrolyte secondary battery, and nonaqueous electrolyte secondary battery
The positive electrode active material with lithium composite oxide A containing W and Ni and W-free lithium composite oxide B containing Ni. Regarding the lithium composite oxide A, the proportion of Ni relative to the total moles of metal elements except for lithium is 30 to 60 mol %, 50% particle size D50 is 2 to 6 μm, 10% particle size D10 is 1.0 μm or more, and 90% particle size D90 is 6.8 μm or less. Regarding the lithium composite oxide B, the proportion of Ni relative to the total moles of metal elements except for lithium is 50 to 95 mol %, 50% particle size D50 is 10 to 22 μm, 10% particle size D10 is 7.0 μm or more, and 90% particle size D90 is 22.5 μm or less. The mass ratio of the lithium composite oxide B to the lithium composite oxide A is 1:1 to 5.7:1.
1. A positive electrode active material for a nonaqueous electrolyte secondary battery, the positive electrode active material comprising lithium composite oxide A containing W and Ni and W-free lithium composite oxide B containing Ni,
wherein, regarding the lithium composite oxide A, the proportion of Ni relative to the total moles of metal elements except for lithium is 30 to 60 mol %, 50% particle size D50 in a cumulative particle size distribution on a volume basis is 2 to 6 μm, 10% particle size D10 in a cumulative particle size distribution on a volume basis is 1.0 μm or more, and 90% particle size D90 in a cumulative particle size distribution on a volume basis is 6.8 μm or less,
regarding the lithium composite oxide B, the proportion of Ni relative to the total moles of metal elements except for lithium is 50 to 95 mol %, 50% particle size D50 in a cumulative particle size distribution on a volume basis is 10 to 22 μm, 10% particle size D10 in a cumulative particle size distribution on a volume basis is 7.0 μm or more, and 90% particle size D90 in a cumulative particle size distribution on a volume basis is 22.5 μm or less, and
a mass ratio of the lithium composite oxide B to the lithium composite oxide A is 1:1 to 5.7:1.
2. The positive electrode active material for a nonaqueous electrolyte secondary battery, according to claim 1 , wherein regarding the lithium composite oxide A, the 50% particle size D50 is 2.5 to 4.5 μm, the 10% particle size D10 is 1.5 to 2.5 μm, and the 90% particle size D90 is 4.5 to 6.0 μm.
3. The positive electrode active material for a nonaqueous electrolyte secondary battery, according to claim 1 , wherein regarding the lithium composite oxide B, the 50% particle size D50 is 11.0 to 21.5 μm, the 10% particle size D10 is 7.0 to 10.5 μm, and the 90% particle size D90 is 21.0 to 22.5 μm.
4. The positive electrode active material for a nonaqueous electrolyte secondary battery, according to claim 1 , wherein at least one of the lithium composite oxide A and the lithium composite oxide B contains Zr.
5. A positive electrode for a nonaqueous electrolyte secondary battery, the positive electrode comprising the positive electrode active material for a nonaqueous electrolyte secondary battery according to claim 1 .
6. A nonaqueous electrolyte secondary battery comprising the positive electrode for a nonaqueous electrolyte secondary battery according to claim 5 .