Disclosed are compositions that may be useful for forming synthetic membranes, methods of forming membranes therefrom, and membranes. In an embodiment, a membrane comprises a free hydrophilic polymer and a polyurethane, the polyurethane comprising a backbone comprising the reaction product of a diisocyanate, a polymeric aliphatic diol, and, optionally, a chain extender, wherein the backbone comprises a C 2 -C 16 fluoroalkyl or C 2 -C 16 fluoroalkyl ether, or the polyurethane comprises an endgroup comprising a C 2 -C 16 fluoroalkyl or C 2 -C 16 fluoroalkyl ether.
1. A method of forming a membrane comprising the steps of:
a. forming a film from a composition comprising from 80 to 99.5 wt %, based on the total weight of the composition, of a solvent and from 0.5 to 20 wt %, based on the total weight of the composition, of a polymer mixture, the polymer mixture comprising:
i. from 65 to 90 wt %, based on the total weight of the polymer mixture, of a polyurethane comprising a backbone comprising the reaction product of:
1. a diisocyanate,
2. a polymeric aliphatic diol component comprising a polycarbonate diol or a polysiloxane diol, and
3. a chain extender, and
wherein the polyurethane comprises an endgroup comprising a C 2 -C 16 fluoroalkyl or C 2 -C 16 fluoroalkyl ether,
ii. from 10 to 35 wt %, based on the total weight of the polymer mixture, of a free hydrophilic polymer having a number average molecular weight of from 5,000 to 5,000,000 g/mol, and
b. evaporating the solvent, thereby forming a membrane.
2. The method according to claim 1 , wherein the polyurethane comprises from 0.1 wt % to 3 wt %, based on the total weight of the polyurethane, of an endgroup comprising a C 2 -C 16 fluoroalkyl or C 2 -C 16 fluoroalkyl ether.
3. The method according to claim 1 , wherein the polymeric aliphatic diol component consists of a polycarbonate diol.
4. The method according to claim 1 , wherein the polymeric aliphatic diol component comprises a polycarbonate diol and a polysiloxane diol.
5. The method according to claim 1 , wherein the polymeric aliphatic diol component consists of a polycarbonate diol and a polysiloxane diol.
6. The method according to claim 1 , wherein the polymeric aliphatic diol component comprises a polycarbonate diol and a poly(tetramethylene oxide) diol.
7. The method according to claim 1 , wherein the polymeric aliphatic diol component consists of a polycarbonate diol and a poly(tetramethylene oxide) diol.
8. The method according to claim 1 , wherein the polymeric aliphatic diol component comprises a polysiloxane diol and a poly(tetramethylene oxide) diol.
9. The method according to claim 1 , wherein the polymeric aliphatic diol component consists of a polysiloxane diol and a poly(tetramethylene oxide) diol.
10. The method according to claim 1 , wherein the diisocyanate is an aliphatic diisocyanate.
11. The method according to claim 1 , wherein the polymeric aliphatic diol component is devoid of hydrophilic polymeric aliphatic diol.
12. The method according to claim 1 , wherein the solvent comprises tetrahydrofuran (THF), methyl-tetrahydrofuran (methyl-THF), or a mixture thereof.
13. The method according to claim 1 , wherein the solvent comprises tetrahydrofuran (THF), methyl-tetrahydrofuran (methyl-THF), or a mixture thereof and wherein a co-solvent is present and comprises methanol, ethanol, isobutanol, propanol, methyl ethyl ketone, or a mixture thereof.
14. The method according to claim 1 , wherein the solvent consists of tetrahydrofuran (THF), methyl-tetrahydrofuran (methyl-THF), or a mixture thereof and optionally a co-solvent consisting of methanol, ethanol, isobutanol, propanol, methyl ethyl ketone, or a mixture thereof.
15. The method according to claim 1 , wherein the solvent comprises 40 wt % or more of tetrahydrofuran (THF), methyl-tetrahydrofuran (methyl-THF), or a mixture thereof, and methanol, ethanol, isobutanol, propanol, methyl ethyl ketone, or a mixture thereof at an amount of from 1 to 60 wt %, based on the total amount of solvent in the composition.
16. The method according to claim 1 , wherein the solvent is present in an amount of 90 wt % to 99 wt %, based on the total weight of the composition.