Reinforced polyproylene composition

1. A polypropylene composition (C) comprising:

(a) 55 to 92 parts per weight of a heterophasic propylene copolymer (HECO);

(b) 1.0 to 10 parts per weight of a polar modified polypropylene (PMP);

(c) 7.0 to 35 parts per weight of carbon fibers (CF);

based on the total parts by weight of compounds (a), (b) and (c),

wherein the intrinsic viscosity (IV) of the xylene soluble (XCS) fraction of the heterophasic propylene copolymer (HECO) is in the range of 3.0 to 4.0 dl/g,

wherein the polypropylene composition (C) has:

(d) a tensile modulus measured according to ISO 527-2 of at least 2500 MPa;

(e) a tensile strength measured according to ISO 527-2 of at least 25 MPa; and

(f) a Charpy Impact Strength measured according to ISO 179-1eU:2000 at 23° C. of at least 35 kJ/m 2 .

2. The polypropylene composition (C) according to claim 1 , wherein the polypropylene composition (C) comprises the heterophasic propylene copolymer (HECO) in an amount of at least 55 wt. %, based on the total weight of the polypropylene composition (C).

3. The polypropylene composition (C) according to claim 1 , wherein the heterophasic propylene copolymer (HECO) has:

(a) a melt flow rate MFR 2 (230° C., 2.16 kg) measured according to ISO 1133 of not more than 60 g/10 min; and/or

(b) a comonomer content of not more than 35 mol %; and/or

(c) a xylene cold solubles (XCS) fraction of not more than 55 wt. %, based on the total weight of the heterophasic propylene copolymer (HECO); and/or

(d) an intrinsic viscosity (IV) of the xylene soluble (XCS) fraction of the heterophasic propylene copolymer (HECO) in the range of 3.0 to 3.5 dl/g; and/or

(e) a comonomer content of the xylene soluble (XCS) fraction of the heterophasic propylene copolymer (HECO) of not more than 65 mol %.

4. The polypropylene composition (C) according to claim 1 , wherein the polypropylene composition (C) comprises the polar modified polypropylene (PMP) in an amount of at least 1.0 wt. %, based on the total weight of the polypropylene composition (C).

5. The polypropylene composition (C) according to claim 1 , wherein the polar modified polypropylene (PMP) comprises groups derived from polar groups selected from the group consisting of acid anhydrides, carboxylic acids, carboxylic acid derivatives, primary and secondary amines, hydroxyl compounds, oxazoline, epoxides, and ionic compounds.

6. The polypropylene composition (C) according to claim 1 , wherein the polar modified polypropylene (PMP) is a propylene polymer grafted with maleic anhydride.

7. The polypropylene composition (C) according to claim 1 , wherein the polypropylene composition (C) comprises the carbon fibers (CF) in an amount of at least 7.0 wt. %, based on the total weight of the polypropylene composition (C).

8. The polypropylene composition (C) according to claim 1 , wherein the heterophasic propylene copolymer (HECO) and the polar modified polypropylene (PMP) are comprised in an amount of at least 57.5 wt. %, based on the total weight of the polypropylene composition (C).

9. The polypropylene composition (C) according to claim 1 , wherein the heterophasic propylene copolymer (HECO), the polar modified polypropylene (PMP) and the carbon fibers (CF) are comprised in an amount of at least 60 wt. %, based on the total weight of the polypropylene composition (C).

10. The polypropylene composition (C) according to claim 1 , wherein the heterophasic propylene copolymer (HECO) comprises:

(a) a polypropylene matrix (M) and

(b) an elastomeric copolymer (E) comprising units derived from propylene and ethylene and/or C 4 to C 20 alpha-olefins.

11. The polypropylene composition (C) according to claim 1 , wherein the polypropylene composition (C) has a tensile elongation at break measured according to ISO 527-2 of at least 6.0%.

12. The polypropylene composition (C) according to claim 1 , wherein the polypropylene composition (C) does not comprise:

(a) any other fibers besides the carbon fibers (CF); and/or

(b) any other polymers besides the heterophasic propylene copolymer (HECO) and the polar modified polypropylene (PMP).

13. An article comprising the polymer composition (C) according to claim 1 .

14. The article according to claim 13 , wherein the article is a molded article or an extruded article.

15. The article according to claim 13 , wherein the article is an automotive article.