Method for impregnating reinforcing fibers with polyaryletherketones and semi-finished products obtained in this way
A process for preparing a semifinished product comprising a PAEK-based resin and reinforcing fibers, including: preparing a dispersion comprising a PAEK-based resin in pulverulent form dispersed in an aqueous phase including at least one volatile organic compound and optionally a surfactant; bringing the reinforcing fibers into contact with said aqueous dispersion; drying the fibers impregnated with dispersion; and heating the impregnated fibers to a temperature sufficient for the melting of the resin, so as to form a semifinished product, wherein the aqueous phase of the dispersion has a dynamic viscosity, measured at 25° C. under a shear stress of 6.8 s −1 on a Brookfield DV2T Extra viscometer, is between 0.1 and 25 Pa·s; and wherein when the surfactant is present, its content is less than 1% by weight relative to the mass of dispersed resin.
1. A process for preparing a semifinished product comprising a PAEK-based resin and reinforcing fibers, comprising the steps of:
a. preparing a dispersion comprising a PAEK-based resin in pulverulent form dispersed in an aqueous phase comprising 1%-40% by weight at least one volatile organic compound and a surfactant;
b. bringing the reinforcing fibers into contact with said aqueous dispersion;
c. drying the fibers impregnated with dispersion; and
d. heating the impregnated fibers to a temperature sufficient for the melting of the resin, so as to form a semifinished product,
wherein the dispersion has a dynamic viscosity, measured at 25° C. under a shear stress of 6.8 s −1 on a Brookfield DV2T Extra viscometer, is between 0.1 and 25 Pa·s; and
wherein the surfactant is present, and its content is less than 1% by weight relative to the mass of dispersed resin.
2. The preparation process as claimed in claim 1 , wherein the volatile organic compound is selected from alcohols, ketones, aldehydes, carboxylic acid esters, glycols and ethers.
3. The preparation process as claimed in claim 1 , wherein the volatile organic compound is an alcohol selected from methanol, ethanol, isopropanol, n-propanol, n-butanol, 2-butanol, tert-butanol, 1-methoxy-2-propanol, 1-ethoxy-2-propanol and mixtures thereof, a glycol selected from ethylene glycol, propylene glycol and mixtures thereof, a ketone such as acetone, an ether, a carboxylic acid ester selected from methyl acetate, ethyl acetate and propyl acetate and mixtures thereof.
4. The preparation process as claimed in claim 1 , wherein the volatile organic compound forms an azeotrope with the water of the aqueous phase.
5. The preparation process as claimed in claim 1 , wherein the reinforcing fibers are carbon fibers.
6. The preparation process as claimed in claim 1 , wherein the dispersion has a dynamic viscosity, measured at 25° C. under a shear stress of 6.8 s −1 on a Brookfield DV2T Extra viscometer, of from 0.1 to 5, Pa·s.
7. The preparation process as claimed in claim 1 , wherein the PAEK resin is selected from the group consisting of poly(ether ketone) (PEK), poly(ether ether ketone) (PEEK), poly(ether ether ketone ketone) (PEEKK), poly(ether ether ketone ketone) (PEKK), poly(ether ketone ether ketone ketone) (PEKEKK), poly(ether ether ketone ether ketone) (PEEKEK), poly(ether ether ether ketone) (PEEEK) and poly(ether diphenyl ether ketone) (PEDEK), mixtures thereof and copolymers thereof with one another or with other members of the family of the PAEKs.
8. The preparation process as claimed in claim 1 , wherein the PAEK resin is a PEKK having a weight percentage of terephthalic units relative to the sum of the terephthalic and isophthalic units of between 35% and 100%.
9. The preparation process as claimed in claim 1 , wherein the pulverulent PAEK resin in the dispersion has a median diameter D50 of from 1 to 300 μm as measured according to the standard ISO 13 320.
10. The preparation process as claimed in claim 1 , wherein the semifinished product is selected from a prepreg or a tape.
11. A semifinished product comprising a PAEK-based resin and reinforcing fibers, capable of being obtained by the process as defined in claim 1 .
12. The semifinished product as claimed in claim 11 , wherein the weight-average molecular weight M w of the PAEK resin, as measured by size exclusion chromatographic analysis, does not increase by more than 100% after heat treatment at 375° C. for 20 minutes.
13. A method of manufacturing a composite material, the method comprising using semifinished product as claimed in claim 11 for the manufacture of composite materials.