Non-random isobutylene copolymers
Non-random isobutylene copolymer includes repeat units derived from isobutylene and one or more comonomers selected from isoprene, butadiene, cyclopentadiene, dicyclopentadiene, limonene, substituted styrenes, and C4 to C10 dienes other than isoprene, butadiene, limonene, cyclopentadiene, or dicyclopentadiene, wherein the molar ratio of isobutylene derived repeat units to the comonomer derived repeat units is from 75:1 to 1.5:1. The non-random copolymers have a molecular weight, Mn, of from 200 to 20,000 Daltons and typically have a high double bond content and a high vinylidene double bond content when diene monomers are utilized.
1. A method of making a non-random isobutylene copolymer comprising:
(a) providing a reaction mixture to a first reactor comprising isobutylene monomer as well as a Lewis acid polymerization catalyst;
(b) polymerizing the reaction mixture in the first reactor while maintaining the first reactor at a temperature above −30° C. and utilizing a first reactor residence time of less than 45 minutes to polymerize at least 30% of the isobutylene monomer fed to the first reactor to produce an isobutylene prepolymer in a polymerization mixture;
(c) feeding the polymerization mixture to a second reactor along with a comonomer selected from isoprene, butadiene, cyclopentadiene, dicyclopentadiene, limonene, substituted styrenes, piperylene and C4 to C10 dienes other than isoprene, butadiene, cyclopentadiene, dicyclopentadiene, limonene or piperylene and optionally additional Lewis acid polymerization catalyst, wherein the molar ratio of isobutylene monomer fed to the first and second reactors to the comonomer is from 60:1 to 1:1;
(d) polymerizing the polymerization mixture and comonomer in the second reactor while maintaining the reactor at a temperature above −30° C. and utilizing a reactor residence time of less than 45 minutes to produce a non-random crude isobutylene copolymer in a copolymerization mixture; and
(e) recovering a purified non-random isobutylene copolymer from the copolymerization mixture having a molecular weight, Mn, of from 200 to 20,000 Daltons.
2. The method according to claim 1 , wherein the first and second reactors are selected from loop reactors, CSTRs and plug flow reactors.
3. A method of making a non-random isobutylene copolymer comprising:
(a) feeding a pre-formed isobutylene homopolymer or oligomer having from 2 to 40 repeat units to a reactor along with a comonomer selected from isoprene, butadiene, cyclopentadiene, dicyclopentadiene, limonene, substituted styrenes, piperylene and C4 to C10 dienes other than isoprene, butadiene, cyclopentadiene, dicyclopentadiene, limonene or piperylene and optionally additional Lewis acid polymerization catalyst and a diluent;
(b) polymerizing the polymer and comonomer mixture in the reactor while maintaining the reactor at a temperature above −30° C. and utilizing a reactor residence time of less than 45 minutes to produce a non-random crude isobutylene copolymer in a copolymerization mixture; and
(c) recovering a purified non-random isobutylene copolymer from the copolymerization mixture having a molecular weight, Mn, of from 200 to 20,000 Daltons;
wherein the molar ratio of isobutylene repeat units to comonomer repeat units in the non-random copolymer is from 60:1 to 1:1.
4. The method according to claim 1 , wherein the reactor(s) are maintained at a temperature of 0° C. or above.
5. The method according to claim 4 , wherein the reactor(s) are maintained at a temperature of 5° C. or above.
6. The method according to claim 1 , utilizing reactor residence times of 20 minutes or less.
7. The method according to claim 1 , wherein the conversion of comonomer is from 45% to 80%.
8. The method according to claim 1 , wherein the Lewis Acid polymerization catalyst comprises BF 3 and an alcohol co-catalyst.
9. The method according to claim 1 , wherein the molar ratio of isobutylene to the one or more comonomers added to the system is from 12:1 to 1:1.
10. The method according to claim 1 , wherein the purified non-random isobutylene copolymer has a molecular weight, Mn, of from 200 to 3000 Daltons.
11. The method according to claim 1 , wherein the comonomer is a diene monomer and the purified non-random isobutylene copolymer has, on average, from 1.25 to 5 double bonds per molecule.
12. The method according to claim 1 , wherein the comonomer is a diene monomer and the purified non-random isobutylene copolymer has, on average, from 0.85 to 2 vinylidene double bonds per molecule.
13. The method according to claim 1 , wherein the comonomer is a diene monomer and the purified non-random isobutylene copolymer has, on average, from 1.2 to 1.8 vinylidene double bonds per molecule.
14. An isobutylene non-random copolymer comprising repeat units derived from isobutylene and a comonomer selected from isoprene, butadiene, cyclopentadiene, dicyclopentadiene, limonene, substituted styrenes, piperylene and C4 to C10 dienes other than isoprene, butadiene, cyclopentadiene, dicyclopentadiene, limonene or piperylene, characterized in that the non-random copolymer exhibits a Tg at least 3.5° C. lower than a like random copolymer polymerized from the same monomer composition.
15. The isobutylene non-random copolymer according to claim 14 , wherein the non-random copolymer exhibits a Tg of from 3.5° C. to 20° C. lower than a like random copolymer polymerized from the same monomer composition.
16. The isobutylene non-random copolymer according to claim 14 , wherein the comonomer comprises isoprene.
17. The isobutylene non-random copolymer according to claim 14 , wherein the comonomer comprises para methyl styrene or alpha methyl styrene.
18. The isobutylene non-random copolymer according to claim 14 , wherein the comonomer comprises butadiene, cyclopentadiene, dicyclopentadiene, limonene, substituted styrenes other than alpha or para methyl styrenes, piperylene and C4 to C10 dienes other than isoprene, butadiene, cyclopentadiene, dicyclopentadiene, limonene or piperylene.
19. The isobutylene non-random copolymer according to claim 14 , wherein the molar ratio of isobutylene-derived repeat units to the comonomer-derived repeat units is from 30:1 to 3:1.
20. The isobutylene non-random copolymer according to claim 14 , wherein the molar ratio of isobutylene-derived repeat units to the comonomer-derived repeat units is from 12.5:1 to 3:1.