NONWOVEN AIR FILTRATION MEDIUM
Air filtration media including synthetic and cellulose fiber layers are provided. More particularly, the air filtration media have high initial efficiency with improved durability, fire retardance, anti-microbial activity, and moisture resistance. The air filtration media can be used in air filters for a variety of applications.
1 . An air filtration medium, comprising:
a first synthetic fiber layer comprising synthetic fibers and having a first FNI of from about 100 ft/(min %) to about 1000 ft/(min %); and
a cellulose fiber layer having a second FNI that is lower than the first FNI, wherein the second FNI is from about 100 ft/(min %) to about 300 ft/(min %).
2 . The air filtration medium of claim 1 , wherein the synthetic fibers comprise bicomponent fibers having an eccentric configuration with a sheath comprising polyethylene and a core comprising PET.
3 . The air filtration medium of claim 2 , wherein the bicomponent fibers have a core to sheath ratio of greater than 1:1.
4 . The air filtration medium of claim 1 , wherein the synthetic fibers comprise bicomponent fibers having an eccentric configuration with a sheath comprising polyethylene and a core comprising polypropylene.
5 . The air filtration medium of claim 1 , wherein the first synthetic fiber layer has a basis weight of from about 5 gsm to about 30 gsm.
6 . The air filtration medium of claim 5 , wherein the first synthetic fiber layer has a basis weight of from about 8 gsm to about 12 gsm.
7 . The air filtration medium of claim 1 , wherein the cellulose fiber layer has a basis weight of from about 25 gsm to about 100 gsm.
8 . The air filtration medium of claim 7 , wherein the cellulose fiber layer has a basis weight of about 25 gsm to about 45 gsm.
9 . The air filtration medium of claim 1 , wherein the first synthetic fiber layer comprises bicomponent fibers having a first length and bicomponent fibers having a second length, wherein the second length is greater than the first length.
10 . The air filtration medium of claim 1 , wherein the cellulose fiber layer comprises modified cellulose fibers.
11 . The air filtration medium of claim 1 , wherein the cellulose fiber layer further comprises bicomponent fibers in amount ranging from about 5 wt-% to about 50 wt-% of the cellulose fiber layer.
12 . The air filtration medium of claim 11 , wherein the bicomponent fibers in the cellulose fiber layer comprise a PET core with a polyethylene sheath and have a dtex of at least about 1.5 dtex.
13 . The air filtration medium of claim 1 , further comprising a binder on an external surface of the cellulose fiber layer.
14 . The air filtration medium of claim 13 , wherein the binder is applied in an amount of from about 3 gsm to about 8 gsm.
15 . The air filtration medium of claim 1 , further comprising a second synthetic fiber layer, disposed between the first synthetic fiber layer and the cellulose fiber layer, having a third FNI that is less than the first FNI and greater than the second FNI.
16 . The air filtration medium of claim 15 , wherein the third FNI is from about 100 ft/(min %) to about 300 ft/(min %).
17 . The air filtration medium of claim 16 , wherein the fibers in the second synthetic fiber layer have a dtex that is less than a dtex of the fibers in the first synthetic fiber layer.
18 . The air filtration medium of claim 17 , wherein the second synthetic fiber layer comprises a blend of cellulose fibers and bicomponent fibers.
19 . The air filtration medium of claim 1 , further comprising a fire suppression layer disposed adjacent to an outer surface of the cellulose fiber layer and comprising fire retardant fibers.
20 . An air filter, comprising a filter housing and the air filtration medium of claim 1 .
21 . The air filter of claim 20 , wherein the air filter has an estimated minimum efficiency reporting value (MERV) of from about 7 to about 9, when tested according to the ASHRAE 52.2 Test Standard.
22 . The air filter of claim 20 , wherein an initial pressure drop across the air filter is from about 0.17″WG to about 0.32″WG, when measured according to the ASHRAE 52.2 Test Standard.
23 . The air filtration medium of claim 1 , wherein, when stored in a water bath or conditioning solution, the air filtration medium has no observable mold after a time period of at least 2 weeks.
24 . The air filtration medium of claim 1 , wherein, when placed in a water bath, the air filtration medium resists full saturation for at least about 5 minutes.