Silane modified polymers with improved properties
The disclosure relates to moisture curable compositions based on a combination of silane-modified polymer and silane functional additive, their manufacture and use. The silane functional additive is preferably prepared from a water miscible polyol having a functionality of about 2 to about 4 and/or a polyol having a tertiary nitrogen atom in the backbone and a functionality equal or greater than about 2.
1. A moisture curable composition comprising a physical blend of:
a moisture curable, silane modified polymer of structure (I)
B(-A n -R—SiXYZ) I (I).
wherein B is an organic polymer backbone and B will not be a siloxane backbone,
A is a divalent linking group linking the polymer backbone to the R 1 group,
I is an integer from 1 to 6,
n is 0 or 1,
R is a divalent C 1 -C 12 hydrocarbon group that optionally comprises a heteroatom,
at least one of X, Y and Z is a hydrolysable group;
a moisture curable, silane functional additive having 3 or more —SiXYZ groups, wherein X, Y and Z are each independently selected from the group consisting of hydrogen, C 1 -C 8 alkyl group, C 1 -C 8 alkoxy group, wherein at least one of the substituents X, Y, Z must be a hydrolyzable group, the silane functional additive being the reaction product of a mixture comprising an isocyanotosilane and a polyol selected from a polyol having a linear ethylene oxide backbone free of nitrogen atoms and a functionality of 3 to 4, a polyol having a linear tetramethylene oxide backbone free of nitrogen atoms and a functionality of 3 to 4, and combinations thereof, wherein the polyol is free of propylene oxide; and
a crosslinker different from the silane modified polymer and the silane functional additive;
wherein cured reaction products of the moisture curable composition have greater strength and greater elongation compared to the moisture curable composition without the moisture curable, silane functional additive.
2. The moisture curable composition of claim 1 wherein B is selected from polyurethane, polyether or polycarbonate.
3. The moisture curable composition of claim 1 wherein the polyol is water miscible.
4. The moisture curable composition of claim 1 wherein A is selected from amide, carbamate, urea, allophanate, biuret, isocyanurate, imino, carboxylate, carbamoyl, am idino, carbonate, sulfonate or sulfinate group or an oxygen or nitrogen atom.
5. The moisture curable composition of claim 1 comprising 20% to 50% silane modified polymer by weight of composition and 10% to 30% of silane functional additive by weight of composition.
6. The moisture curable composition of claim 1 wherein X, Y and Z are each independently selected from H, C 1 -C 8 alkyl group, C 1 -C 8 alkoxy group or C 1 -C 8 acyloxy group, with the proviso that at least one of the groups X, Y, Z must be the alkoxy group or the acryloxy group.
7. The moisture curable composition of claim 1 wherein the cured reaction product has the silane functional additive covalently bonded to the silane modified polymer in the form of a crosslinked network.
8. The moisture curable composition of claim 1 wherein the silane functional additive is the reaction product of the isocyanotosilane and the polyol has a linear ethylene oxide backbone and a functionality of about 3.
9. The moisture curable composition of claim 1 wherein the polyol is selected from a polyol having a linear ethylene oxide backbone and a functionality of about 3, the polyol comprising three, linear ethylene oxide portions with each ethylene oxide portion having a terminal OH moiety.
10. The moisture curable composition of claim 1 being substantially free of tin or other metal catalyst.
11. Cured reaction products of the curable composition of claim 1 .
12. An article having a surface and comprising cured reaction products of the curable composition of claim 1 bonded to the surface.
13. The moisture curable composition of claim 1 wherein the polyol used to prepare the silane functional additive reaction product is selected from a triol comprising three separate ethylene oxide portions each terminated by a hydroxyl group, trimethylolpropane ethoxylate, glycerol ethoxylate and combinations thereof.
14. The moisture curable composition of claim 1 wherein the polyol used to prepare the silane functional additive reaction product comprises polytetramethylene oxide units.