Rolling slide member, rolling bearing using same, and method for manufacturing rolling slide member
A rolling-sliding member that is high in hardness and continues to have a passivation film reliably even after being subjected to a process that does not require any processing for removal of scale, etc., as well as a rolling bearing using the same and a method for manufacturing the rolling-sliding member.
1. A method for manufacturing a rolling-sliding member, wherein the rolling-sliding member is an outer ring of a rolling bearing, the outer ring having an outer circumferential surface, an inner surface and side surfaces on each side of the outer ring between the outer circumferential surface and the inner surface, the method comprising:
performing vacuum heat treatment, to attain hardness of 55 HRC or higher, on the outer ring of the rolling bearing, the outer ring being comprised of:
0.15 mass % or larger and smaller than 0.70 mass % of C;
0.05 to 1.00 mass % of Si;
0.05 to 1.00 mass % of Mn;
0.03 mass % or smaller of P;
0.03 mass % or smaller of S;
0.001 to 0.500 mass % of Cu;
0.05 to 0.50 mass % of Ni;
11 to 18.0 mass % of Cr;
0.05 to 2.00 mass % of Mo;
0.01 to 0.50 mass % of W;
0.01 to 0.50 mass % of V;
0.05 to 0.40 mass % of N;
0.02 mass % or smaller of O;
0.080 mass % or smaller of Al;
0.0005 to 0.0050 mass % of B;
provided that the total content of C and N is larger than 0.4 mass % and smaller than 0.7 mass %, and a content ratio C/N is 0.75 or larger; and
the remainder being Fe and unavoidable impurities;
wherein the vacuum heat treatment forms a Cr-deficient layer in a surface layer part of the outer ring of the rolling bearing; and
thereafter performing processing of removing the surface layer part of the outer circumferential surface and the side surfaces of the outer ring of the rolling bearing such that no Cr-deficient layer exists on the outer circumferential surface and the side surfaces of the outer ring of the rolling bearing, but a Cr-deficient layer exists on the inner surface of the outer ring of the rolling bearing.
2. The method for manufacturing a rolling-sliding member according to claim 1 , wherein a region of performing the processing of removing the surface layer part is a region having a depth of at least 40 nm from the outer circumferential surface and the side surfaces of the outer ring of the rolling bearing.