Anti-fog and anti-reflective dual-functional coating for optical articles
A coating for an optical article, such as a lens, includes a bottom coating having at least one hydrophilic resin binder and at least one surfactant, forming an anti-fogging layer, and a top coating overlying the bottom coating, forming an anti-reflective layer. The top coating includes nanopores, which may be less than 150 nm in size.
1. A method of making an optical article, comprising:
applying a bottom coating composition to a top surface of the optical article, the bottom coating composition comprising at least one hydrophilic resin binder;
applying a top coating composition over the bottom coating composition, the top coating composition comprising nanopores and nanoparticles; and
curing the bottom coating composition and the top coating composition in a single curing step, a cured bottom coating forming an anti-fogging layer and a cured top coating forming an anti-reflective layer on the top surface of the optical article.
2. The method of claim 1 , wherein the nanopores have less than 150 nm pore size.
3. The method of claim 1 , wherein the cured top coating further comprises a porosity from about 30% to about 90%.
4. The method of claim 1 , wherein the nanoparticles have a diameter ranging in size from about 1 to about 150 nm dispersed in a solvent.
5. The method of claim 1 , wherein applying the top coating composition over the bottom coating composition is done by a method selected from the group consisting essentially of sol-gel dip-coating, chemical bath deposition, oblique angle evaporation, layer-by-layer assembly, and soft-templated solvent deposition.
6. The method of claim 1 , further comprising:
applying the bottom coating composition to a bottom surface of the optical article;
applying the top coating composition over the bottom coating composition on the bottom surface of the optical article; and
curing the bottom coating composition and the top coating composition in a single curing step.
7. The method of claim 1 , wherein the top coating composition further comprises a transparent, dielectric and non-water-soluble compound selected from the group consisting essentially of oxides, nitrides and sulfides.
8. An optical article, comprising:
an optical substrate having a top surface and a bottom surface;
a bottom coating overlying the top surface and the bottom surface of the optical substrate, forming an anti-fogging layer; and
a top coating overlying the bottom coating, the top coating forming an anti-reflective layer,
wherein the bottom coating and the top coating are obtained by applying a bottom coating composition comprising at least one hydrophilic resin binder, applying a top coating composition comprising nanopores and nanoparticles, and curing the bottom coating composition and the top coating composition in a single curing step.
9. The optical article of claim 8 , wherein the nanopores have less than 150 nm pore size.
10. The optical article of claim 8 , wherein the top coating further comprises a porosity from about 30% to about 90%.
11. The optical article of claim 8 , wherein the nanoparticles have a diameter ranging in size from about 1 to about 150 nm dispersed in a solvent.
12. The optical article of claim 8 , wherein the top coating composition is applied to the optical substrate by a method selected from the group consisting essentially of sol-gel dip-coating, chemical bath deposition, oblique angle evaporation, layer-by-layer assembly, and soft-templated solvent deposition.
13. A coating for an optical article, comprising:
a cross-linked bottom coating, forming an anti-fogging layer; and
a cross-linked top coating overlying the bottom coating, forming an anti-reflective layer, wherein the cross-linked bottom coating and the cross-linked top coating are obtained by applying a cross-linkable bottom coating composition comprising at least one hydrophilic resin binder, applying a cross-linkable top coating composition comprising nanopores and nanoparticles, and curing the cross-linkable bottom coating composition and the cross-linkable top coating composition in a single curing step.
14. The coating of claim 13 , wherein the nanopores have less than 150 nm pore size.
15. The coating of claim 13 , wherein the cross-linked top coating further comprises a porosity from about 30% to about 90%.
16. The coating of claim 13 , wherein the nanoparticles have a diameter ranging in size from about 1 to about 150 nm dispersed in a solvent.
17. The coating of claim 13 , wherein the cross-linkable top coating composition further comprises a transparent, dielectric and non-water-soluble compound selected from the group consisting essentially of oxides, nitrides and sulfides.
18. The coating of claim 13 , wherein the binder is selected from the group consisting essentially of: polyurethane, acrylic, polysiloxane, epoxy, polyvinyl alcohol, polyvinylpyrrolidone, polyethylene glycol, and combinations and hybrids thereof.
19. The coating of claim 13 , wherein a thickness of the cross-linked top coating is from about 70 to about 200 nm.
20. The coating of claim 13 , wherein a thickness of the cross-linked bottom coating is from about 2 to about 25 microns.