LOW BASIS WEIGHT INKJET PRINTABLE SUBSTRATES WITH LOWER SHOWTHROUGH AND IMPROVED WATERFASTNESS AND PRINT DENSITY
A method for preparing a printable substrate having a showthrough value of about 0.14 or less, and an opacity value of at least about 88% which includes a paper substrate with a first and second surfaces formed of paper fibers having a basis weight of from about 12 to about 32 lbs/1300 ft 2 , and a substrate filler in an amount in the range of from 0 to about 30% by weight of the paper substrate; and a surface size layer on at least one of the first and second surfaces, the surface size layer having about 50 lbs or less per ton of the paper substrate of a starch surface sizing agent and a multivalent metal salt drying agent in an amount sufficient to impart to the at least one of the first and second surfaces a black print density value of at least about 0.8 when inkjet printed with pigmented inks and a waterfastness value of at least about 85% when inkjet printed with dye-based inks, the printable substrate having a MD tensile strength of at least about 12 lbs/in. and a CD tensile strength of at least about 6 lbs/in.
1 . A method for preparing a printable substrate, which comprises the following steps:
(a) providing a paper substrate having a first surface and a second surface and having a basis weight of from about 12 to about 32 lbs/1300 ft 2 , the paper substrate comprising:
paper fibers in an amount in the range of from about 60 to 100% by weight of the paper substrate; and
a substrate filler in an amount in the range of from 0 to about 30% by weight of the paper substrate; and
(b) forming on at least one of the first and second surfaces a surface size layer to provide the printable substrate having a showthrough value of about 0.14 or less, and an opacity value of at least about 88%;
(c) wherein the surface size layer of step (b) comprises about 50 lbs or less per ton of the paper substrate of a starch surface sizing agent;
(d) wherein the surface size layer of step (b) comprises a multivalent metal salt drying agent in an amount sufficient to impart to the at least one of the first and second surfaces a black print density value of at least about 0.8 when inkjet printed with pigmented inks and a waterfastness value of at least about 85% when inkjet printed with dye-based inks;
(e) wherein the printable substrate of step (b) has a MD tensile strength of at least about 12 lbs/in. and a CD tensile strength of at least about 6 lbs/in.
2 . The method of claim 1 , wherein a surface size layer is formed on both the first and second surfaces during step (b).
3 . The method of claim 1 , wherein step (b) is carried out by applying a surface size composition comprising the multivalent metal salt drying agent and the optional starch surface sizing agent to at least one of the first and second surfaces with a size press to form the surface size layer.
4 . The method claim 1 , wherein the size press is a rod metering size press.
5 . The method of claim 1 , wherein the size press is flooded nip size press.
6 . The method of claim 1 , wherein the substrate filler comprises from about 10 to about 25% by weight of the paper substrate of step (a).
7 . The method of claim 6 , wherein the substrate filler comprises from about 15 to about 20% by weight of the paper substrate of step (a).
8 . The method of claim 1 , wherein the substrate filler of step (a) comprises calcium carbonate.
9 . The method of claim 1 , wherein the paper substrate of step (a) comprises cationic starch binder in the range of from about 0.05 to about 3% by weight of the paper substrate.
10 . The method of claim 9 , wherein the paper substrate of step (a) comprises cationic starch binder in the range of from about 0.1 to about 2% by weight of the paper substrate.
11 . The method of claim 1 , wherein the surface size layer formed during step (b) comprises from about 0.1 to about 10 lbs or less per ton of the paper substrate of a starch surface sizing agent.
12 . The method of claim 1 , wherein the starch surface sizing agent comprises ethylated starch.
13 . The method of claim 1 , wherein the paper substrate of step (a) comprises about 10 to about 40% by weight softwood fibers and from about 60 to about 90% by weight hardwood fibers.