Malleable demineralized bone composition and method of manufacture
A malleable demineralized bone composition consists of cortical bone made from a first portion and a second portion. The first portion and second portion of cortical bone is made from cut pieces freeze dried then ground into particles and demineralized then freeze-dried. A volume of the second portion is placed in a solution of sterile water to create a mixture, the water volume being seven times the volume of the second portion, the mixture is autoclaved under heat and pressure to form a gelatin, and the first portion is mixed with the gelatin to form a malleable putty or paste.
1. A method of making a malleable demineralized bone composition consisting of cortical bone comprises the steps of:
preparing cortical bone by cutting the cortical bone into pieces, freeze-drying the pieces and then grinding into particles to a particle size up to 300 microns and demineralizing the ground particles and freeze-drying the demineralized ground particles to form freeze-dried DBM particles;
dividing the freeze-dried DBM particles into a first portion and a second portion;
autoclaving a volume of the second portion of DBM particles mixed with sterile water in a 7:1 ratio by volume for a predetermined time at a pre-set temperature and pressure to form a gelatin;
cooling the gelatin made from the second portion; and
mixing the freeze-dried ground particles of the first portion with the gelatin from the second portion at a ratio of 80:20 or less gelatin to DBM to create a malleable and cohesive paste, wherein the malleable and cohesive paste is moldable into different shapes with no visible cracks and maintains its shape while immersed in normal saline or water for a minimum of one minute.
2. The method of making a malleable demineralized bone composition of claim 1 wherein the demineralized particles are freeze-dried at −80 degrees C. for over 30 hours.
3. The method of making a malleable demineralized bone composition of claim 1 wherein the cut pieces of cortical bone having a width, a length and a thickness in the range of 1 to 4 mm.
4. The method of making a malleable demineralized bone composition of claim 1 wherein the sterile water and second portion of DBM particles are autoclaved for 1.25 hours.
5. The method of making a malleable demineralized bone composition of claim 1 wherein the autoclaving includes 15 minutes of conditioning, 30 minutes exposure at 121.1 degrees C. at a pressure of 30.14 psi; and 30 minutes of drying.
6. The method of making a malleable demineralized bone composition of claim 1 wherein the ratio of gelatin to particles from the first portion is 80:20 by volume.
7. The method of making a malleable demineralized bone composition of claim 1 wherein the mixture formed as a malleable and cohesive paste is packaged in a capped syringe.
8. The method of making a malleable demineralized bone composition of claim 7 wherein the packaged mixture is sterilized using E-beam irradiation and stored at room temperature.