Additive manufacturing of articles comprising beryllium
A method of making an article includes depositing a plurality of layers to form a three-dimensional preform, sintering the preform to form a sintered preform, and infiltrating the preform with at least one metal to form the article. At least one layer of the plurality of layers is formed from a beryllium-containing composition including beryllium powder. The infiltrating metal can be selected from aluminum and magnesium.
1. A beryllium-containing composite that is an additive manufactured article, the composite comprising:
a three-dimensional porous beryllium-containing sintered preform consisting of a plurality of interconnected beryllium-containing deposition layers and a plurality of sintered preform voids, and
an infiltrating metal matrix disposed within the plurality of sintered preform voids, wherein the infiltrating metal matrix includes beryllium, aluminum, magnesium, alloys thereof, or combinations thereof; and
wherein the additive manufactured article has a composition of Al—Be, Mg—Be, Al—Mg—Be, Al—Be—Ni, Al—Mg—Be—Ni, or combinations thereof.
2. The composite of claim 1 , wherein the three-dimensional porous beryllium-containing sintered preform includes beryllium and at least one of nickel, aluminum, alloys thereof, or combinations thereof.
3. The composite of claim 2 , wherein the sintered preform includes from zero to 8 wt % nickel.
4. The composite of claim 2 , wherein the sintered preform includes from 35 wt % to 65 wt % beryllium and from 35 wt % to 65 wt % aluminum.
5. The composite of claim 1 , wherein the infiltrating metal matrix is aluminum.
6. The composite of claim 1 , wherein the infiltrating metal matrix is magnesium.
7. The composite of claim 1 , wherein the composite has a composition of from 0 wt % to 5 wt % nickel, from 58 wt % to 65 wt % beryllium, and from 30 wt % to 42 wt % aluminum.
8. The composite of claim 1 , wherein the composite demonstrates a density of about 1.5 g/cc to about 2.5 g/cc.
9. The composite of claim 1 , wherein the composite demonstrates a coefficient of thermal expansion at 25° C. of from about 5 ppm/° C. to about 25 ppm/° C.
10. The composite of claim 1 , wherein the composite demonstrates an elastic modulus of from 100 GPa to 300 GPa.
11. The composite of claim 1 , wherein the composite demonstrates a yield strength of from 150 to 900 MPa.
12. The composite of claim 1 , wherein the composite demonstrates an ultimate tensile strength of from 170 MPa to 1000 MPa.
13. The composite of claim 1 , wherein the composite is finished by coating, polishing, plating, or combinations thereof.
14. The composite of claim 13 , wherein the composite includes a protective coating of aluminum, cadmium, nickel, or combinations thereof.
15. The composite of claim 14 , wherein the composite includes a protective coating of aluminum.
16. The composite of claim 1 , wherein the composite is weldable.
17. The composite of claim 1 , wherein the three-dimensional porous beryllium-containing sintered preform is a majority by weight beryllium.
18. The composite of claim 1 , wherein each beryllium-containing deposition layer consists of less than 100 wt % beryllium and from greater than zero wt % to about 8 wt % nickel.
19. The composite of claim 1 , wherein beryllium particles in the interconnected beryllium-containing deposition layers are metallurgically bonded together.